CYCOLOY? CX7010 resin
聚碳酸酯+丙烯腈丁二烯苯乙烯
产品说明:
CYCOLOY CX7010 resin is an injection moldable PC/ABS blend. It contains non-brominated and non-chlorinated flame retardant systems to meet UL-94 V0. Excellent flow combined with good balance of properties and all color options make CYCOLOY CX7010 an ideal candidate for a wide variety of large size molding, thin wall applications.
| 总体 | ||||
|
材料状态
|
|
|||
|
资料1
|
||||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
添加剂
|
|
|||
|
特性
|
|
|||
|
用途
|
|
|||
|
外观
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.18
|
g/cm3
|
ASTM D792,ISO 1183 |
|
熔流率（熔体流动速率）(260°C/2.16 kg)
|
22
|
g/10 min
|
ASTM D1238 |
|
溶化体积流率（MVR）(260°C/2.16 kg)
|
18.0
|
cm3/10min
|
ISO 1133 |
|
收缩率 - 流动(3.20 mm)
|
0.40 到 0.60
|
%
|
内部方法 |
|
吸水率
|
ISO 62 | ||
|
饱和, 23°C
|
0.20
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.10
|
%
|
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
--2
|
2950
|
MPa
|
ASTM D638 |
|
--
|
2750
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服3
|
66.0
|
MPa
|
ASTM D638 |
|
屈服
|
68.0
|
MPa
|
ISO 527-2/50 |
|
断裂3
|
45.0
|
MPa
|
ASTM D638 |
|
断裂
|
40.0
|
MPa
|
ISO 527-2/50 |
|
伸长率
|
|||
|
屈服3
|
3.4
|
%
|
ASTM D638 |
|
屈服
|
3.8
|
%
|
ISO 527-2/50 |
|
断裂3
|
35
|
%
|
ASTM D638 |
|
断裂
|
15
|
%
|
ISO 527-2/50 |
|
弯曲模量
|
|||
|
50.0 mm 跨距4
|
2850
|
MPa
|
ASTM D790 |
|
--5
|
2600
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
--5,6
|
100
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距4
|
110
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度7
|
ISO 179/1eA | ||
|
-30°C
|
5.0
|
kJ/m2
|
|
|
23°C
|
10
|
kJ/m2
|
|
|
悬壁梁缺口冲击强度
|
|||
|
-30°C
|
50
|
J/m
|
ASTM D256 |
|
23°C
|
75
|
J/m
|
ASTM D256 |
|
-30°C8
|
5.0
|
kJ/m2
|
ISO 180/1A |
|
23°C8
|
10
|
kJ/m2
|
ISO 180/1A |
|
装有测量仪表的落镖冲击(23°C, Total Energy)
|
40.0
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
1.8 MPa, 未退火, 3.20 mm
|
74.0
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 6.40 mm
|
84.0
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 64.0 mm 跨距9
|
77.0
|
°C
|
ISO 75-2/Af |
|
维卡软化温度
|
|||
|
--
|
91.0
|
°C
|
ASTM D152510 |
|
--
|
90.0
|
°C
|
ISO 306/B50 |
|
--
|
95.0
|
°C
|
ISO 306/B120 |
|
Ball Pressure Test(75°C)
|
Pass
|
|
IEC 60695-10-2 |
|
线形热膨胀系数
|
|||
|
流动 : -40 到 40°C
|
6.0E-5
|
cm/cm/°C
|
ASTM E831 |
|
流动 : -40 到 40°C
|
7.5E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
横向 : -40 到 40°C
|
6.0E-5
|
cm/cm/°C
|
ASTM E831 |
|
横向 : -40 到 40°C
|
7.5E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
导热系数
|
0.20
|
W/m/K
|
ISO 8302 |
|
RTI Elec
|
60.0
|
°C
|
UL 746 |
|
RTI Imp
|
60.0
|
°C
|
UL 746 |
|
RTI
|
60.0
|
°C
|
UL 746 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
1.0E+15
|
ohm
|
IEC 60093 |
|
体积电阻率
|
1.0E+15
|
ohm·cm
|
IEC 60093 |
|
介电强度
|
IEC 60243-1 | ||
|
0.800 mm, 在油中
|
35
|
kV/mm
|
|
|
1.60 mm, 在油中
|
25
|
kV/mm
|
|
|
3.20 mm, 在油中
|
17
|
kV/mm
|
|
|
高电弧燃烧指数(HAI)
|
PLC 0
|
|
UL 746 |
|
热丝引燃 (HWI)
|
PLC 3
|
|
UL 746 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级(1.50 mm)
|
V-0
|
|
UL 94 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
77.0 到 82.0
|
°C
|
|
|
干燥时间
|
2.0 到 4.0
|
hr
|
|
|
干燥时间，最大
|
8.0
|
hr
|
|
|
建议的最大水分含量
|
0.040
|
%
|
|
|
建议注射量
|
30 到 80
|
%
|
|
|
料筒后部温度
|
221 到 249
|
°C
|
|
|
料筒中部温度
|
227 到 260
|
°C
|
|
|
料筒前部温度
|
232 到 266
|
°C
|
|
|
射嘴温度
|
232 到 266
|
°C
|
|
|
加工（熔体）温度
|
232 到 266
|
°C
|
|
|
模具温度
|
60.0 到 82.0
|
°C
|
|
|
背压
|
0.345 到 0.689
|
MPa
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
0.038 到 0.076
|
mm
|
| 备注 |
  |