上海沐音新材料有限公司
CYCOLOY? CM6240 resin
聚碳酸酯+丙烯腈丁二烯苯乙烯
产品说明:
CYCOLOY CM6240 resin is a flame retardant PC/ABS blend featuring balanced properties of high modulus, good flow and ductility. It is of Br- Cl-free flame retardant systems intended to meet thin wall flame resistance and various environmental requirements.
| 总体 | ||||
|
材料状态
|
|
|||
|
资料1
|
||||
|
UL 黄卡2
|
||||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
特性
|
|
|||
|
用途
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.30
|
g/cm3
|
ASTM D792,ISO 1183 |
|
熔流率（熔体流动速率）(260°C/2.16 kg)
|
17
|
g/10 min
|
ASTM D1238 |
|
溶化体积流率（MVR）(260°C/2.16 kg)
|
15.0
|
cm3/10min
|
ISO 1133 |
|
收缩率
|
内部方法 | ||
|
流动
|
0.33
|
%
|
|
|
流动 : 3.20 mm
|
0.30 到 0.40
|
%
|
|
|
横向流动
|
0.38
|
%
|
|
|
吸水率
|
ISO 62 | ||
|
饱和, 23°C
|
0.10
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.030
|
%
|
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
--3
|
4350
|
MPa
|
ASTM D638 |
|
--
|
4460
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服4
|
55.0
|
MPa
|
ASTM D638 |
|
屈服
|
56.0
|
MPa
|
ISO 527-2/5 |
|
断裂4
|
40.0
|
MPa
|
ASTM D638 |
|
断裂
|
29.0
|
MPa
|
ISO 527-2/5 |
|
伸长率
|
|||
|
屈服4
|
3.0
|
%
|
ASTM D638 |
|
屈服
|
3.0
|
%
|
ISO 527-2/5 |
|
断裂4
|
35
|
%
|
ASTM D638 |
|
断裂
|
25
|
%
|
ISO 527-2/5 |
|
弯曲模量
|
|||
|
50.0 mm 跨距5
|
4400
|
MPa
|
ASTM D790 |
|
--6
|
4510
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
--6,7
|
101
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距5
|
96.0
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度8(23°C)
|
6.0
|
kJ/m2
|
ISO 179/1eA |
|
悬壁梁缺口冲击强度
|
|||
|
-30°C
|
60
|
J/m
|
ASTM D256 |
|
23°C
|
86
|
J/m
|
ASTM D256 |
|
-30°C9
|
7.0
|
kJ/m2
|
ISO 180/1A |
|
23°C9
|
7.0
|
kJ/m2
|
ISO 180/1A |
|
装有测量仪表的落镖冲击
|
ASTM D3763 | ||
|
-30°C, Total Energy
|
35.0
|
J
|
|
|
23°C, Total Energy
|
56.0
|
J
|
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
1.8 MPa, 未退火, 6.40 mm
|
90.0
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 64.0 mm 跨距10
|
86.0
|
°C
|
ISO 75-2/Af |
|
维卡软化温度
|
|||
|
--
|
97.0
|
°C
|
ASTM D152511,ISO 306/B5011 |
|
--
|
100
|
°C
|
ISO 306/B120 |
|
线形热膨胀系数
|
|||
|
流动 : -40 到 40°C
|
4.9E-5
|
cm/cm/°C
|
ASTM E831 |
|
流动 : -40 到 40°C
|
4.8E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
横向 : -40 到 40°C
|
6.4E-5
|
cm/cm/°C
|
ASTM E831 |
|
横向 : -40 到 40°C
|
6.3E-5
|
cm/cm/°C
|
ISO 11359-2 |
| 可燃性 |
额定值
|
|
测试方法
|
|
UL 阻燃等级
|
UL 94 | ||
|
0.800 mm, Testing by SABIC
|
V-0
|
|
|
|
1.50 mm, Testing by SABIC
|
5VB
|
|
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
80.0 到 90.0
|
°C
|
|
|
干燥时间
|
4.0 到 6.0
|
hr
|
|
|
干燥时间，最大
|
16
|
hr
|
|
|
建议的最大水分含量
|
0.040
|
%
|
|
|
料筒后部温度
|
220 到 255
|
°C
|
|
|
料筒中部温度
|
230 到 275
|
°C
|
|
|
料筒前部温度
|
255 到 285
|
°C
|
|
|
射嘴温度
|
255 到 285
|
°C
|
|
|
加工（熔体）温度
|
255 到 285
|
°C
|
|
|
模具温度
|
70.0 到 95.0
|
°C
|
| 备注 |
  |