东莞市广裕塑胶原料有限公司
美国NatureWorks食品级PLA 3001D 清晰透明,食品级，一次性餐具 化妆品包装应用，食品级PLA.
Ingeo? 3100HP
聚乳酸
NatureWorks? LLC
产品说明：
Ingeo 3100HP is a medium viscosity product from NatureWorks LLC, designed for medium flow injection molding applications. It is designed to crystallize during processing, leading to higher heat deflection temperatures in opaque applications.
The variety of products made with 3100HP is widely varied and growing. Applications include disposables such as cutlery, cups, plates, cosmetic packaging, and durables such as electronics housings and semi-durable building materials.
Ingeo? 3100HP 物性表
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.24 | g/cm3 | ASTM D792 |
| 熔流率（熔体流动速率）(210°C/2.16 kg) | 24 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 | |||
| --1 | 1.7 到 1.8 | % | |
| --2 | 0.20 到 0.40 | % | |
| Relative Viscosity3 | 3.1 | ASTM D5225 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 | ASTM D638 | ||
| 屈服4 | 64.1 | MPa | ASTM D638 |
| 屈服5 | 64.8 | MPa | ASTM D638 |
| 伸长率 | ASTM D638 | ||
| 断裂6 | 2.2 | % | ASTM D638 |
| 断裂7 | 3.4 | % | ASTM D638 |
| 弯曲模量 | ASTM D790 | ||
| --8 | 4360 | MPa | ASTM D790 |
| --9 | 3590 | MPa | ASTM D790 |
| 弯曲强度 | ASTM D790 | ||
| --10 | 108 | MPa | ASTM D790 |
| --11 | 112 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 | ASTM D256 | ||
| --12 | 32 | J/m | ASTM D256 |
| --13 | 18 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 | ASTM E2092 | ||
| 0.45 MPa, 未退火14 | 149 | °C | ASTM E2092 |
| 0.45 MPa, 未退火15 | 54.0 | °C | ASTM E2092 |
| 结晶峰温度 (DSC)16 | 180 | °C |
| 光学性能 | 额定值 | ||
|---|---|---|---|
| Clarity | |||
| --17 | Opaque | ||
| --18 | Transparent |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 建议的最大水分含量 | 0.025 | % | |
| 料斗温度 | 21.1 | °C | |
| 料筒后部温度 | 185 | °C | |
| 料筒中部温度 | 195 | °C | |
| 料筒前部温度 | 200 | °C | |
| 射嘴温度 | 200 | °C | |
| 加工（熔体）温度 | 199 | °C | |
| 模具温度 | 120 | °C | |
| 背压 | 1.72 | MPa | |
| 螺杆转速 | 200 | rpm |
| 注射说明 |
|---|
| Note: Amorphous polymer must be dried below 120F (50C). |
| 备注 | |
|---|---|
| 1 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil Fat) |
| 2 . | Molded amorphous with 26°C mold temperature |
| 3 . | Measured at 1.0 g/dL in chloroform at 30°C |
| 4 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil Fat) |
| 5 . | Molded amorphous with 26°C mold temperature |
| 6 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil Fat) |
| 7 . | Molded amorphous with 26°C mold temperature |
| 8 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil Fat) |
| 9 . | Molded amorphous with 26°C mold temperature |
| 10 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil Fat) |
| 11 . | Molded amorphous with 26°C mold temperature |
| 12 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil Fat) |
| 13 . | Molded amorphous with 26°C mold temperature |
| 14 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil Fat) |
| 15 . | Molded amorphous with 26°C mold temperature |
| 16 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil Fat) |
| 17 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil Fat) |
| 18 . | Molded amorphous with 26°C mold temperature |