东莞市广裕塑胶原料有限公司
TPU A92P4637 抗菌 抗微生物 食品级TPU FDA USP认证 食品医疗应用。
IROGRAN? A 92 P 4637
热塑性聚氨酯弹性体（聚醚）
Huntsman Corporation
产品说明：
IROGRAN A 92 P 4637 is a thermoplastic polyether-polyurethane for injection moulding and extrusion applications.
Additional characteristics of the product are excellent microbial resistance, high low-temperature flexibility, especially suitable for cable jacket.
PERFORMANCE FEATURES
Additional characteristics of the product are excellent microbial resistance, high low-temperature flexibility, especially suitable for cable jacket.
PERFORMANCE FEATURES
- Excellent hydrolysis resistance
- High microbial resistance
- High stability of melt
- Easy coloring
- Low-temperature flexibility
IROGRAN? A 92 P 4637 物性表
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重1 | 1.13 | g/cm3 | |
| 溶化体积流率（MVR）(190°C/21.6 kg) | 55.0 | cm3/10min | |
| 收缩率 | |||
| 流动 | 0.40 | % | ASTM D955 |
| -- | 0.90 | % |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 | ASTM D2240, ISO 868 | ||
| 邵氏 A, 注塑 | 92 | ASTM D2240, ISO 868 | |
| 邵氏 D, 注塑 | 39 | ASTM D2240, ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| Abrasion2 | 30 | mm3 | ISO 4649 |
| 弹性体 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸应力3 | |||
| 100%应变 | 8.96 | MPa | ASTM D412 |
| 100%应变 | 9.10 | MPa | DIN 53504 |
| 300%应变 | 14.1 | MPa | ASTM D412 |
| 300%应变 | 15.9 | MPa | DIN 53504 |
| 抗张强度4 | |||
| 断裂 | 33.6 | MPa | ASTM D412 |
| 断裂 | 45.0 | MPa | DIN 53504 |
| 伸长率5 | |||
| 断裂 | 670 | % | ASTM D412 |
| 断裂 | 600 | % | DIN 53504 |
| 撕裂强度6 | |||
| -- | 116 | kN/m | ASTM D624 |
| -- | 74 | kN/m | ISO 34-1 |
| 压缩永久变形7 | ASTM D395, ISO 815 | ||
| 23°C, 24 hr | 25 | % | ASTM D395, ISO 815 |
| 70°C, 24 hr | 41 | % | ASTM D395, ISO 815 |
| 巴肖氏弹性 | 34 | % |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | |||
| -- | 100 到 110 | °C | |
| 真空干燥机 | 80.0 到 90.0 | °C | |
| 干燥时间 | |||
| -- | 3.0 | hr | |
| 真空干燥机 | 3.0 | hr | |
| Dew Point | -30.0 | °C | |
| 料筒后部温度 | 175 到 195 | °C | |
| 料筒中部温度 | 175 到 195 | °C | |
| 料筒前部温度 | 175 到 195 | °C | |
| 射嘴温度 | 180 到 200 | °C | |
| 加工（熔体）温度 | 170 到 195 | °C | |
| 模具温度 | 20.0 到 70.0 | °C |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 100 到 110 | °C | |
| 干燥时间 | 3.0 | hr | |
| 料筒温度 | 25.0 到 40.0 | °C | |
| 料筒1区温度 | 165 到 190 | °C | |
| 料筒2区温度 | 165 到 190 | °C | |
| 料筒3区温度 | 165 到 190 | °C | |
| 料筒4区温度 | 165 到 190 | °C | |
| 料筒5区温度 | 165 到 190 | °C | |
| 接头温度 | 175 到 195 | °C | |
| 口模温度 | 175 到 200 | °C |
| 备注 | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Injection Molded |
| 4 . | Injection Molded |
| 5 . | Injection Molded |
| 6 . | Injection Molded |
| 7 . | Injection Molded |