苏州天涛塑化有限公司
原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | ASTM D-570 | 0.3 | % | |
| 假密度 | ASTM D-1182 | 0.77 | g/cm3 | ||
| 物理性能 | 流动系数 | ASTM D-1238 | 8.0 | g/10min | |
| 比重 | ASTM D-792 | 1.19 | |||
| 全光透过率 | ASTM D-1003 | 92 | % | ||
| 机械性能 | 曲折率 | ASTM D-542 | 1.491 | ||
| 弯曲强度 | ASTM D-790/PSI | 14200/1000 | Kg/cm2 | ||
| 硬度 | ASTM D-790 | M-85 | |||
| 引张强度 | ASTM D-638/PSI | 9700/680 | Kg/cm2 | ||
| 成型收缩率 | ASTM D-955 | 0.002-0.006 | mm/mm | ||
| 抗冲击力 | ASTM D-256 | 0.37 | ft-lbs/in2 | ||
| 延伸率 | ASTM D-638 | 5.0 | % | ||
| 抗冲击力 | ASTM D-256 | 2.0 | kg-cm/cm | ||
| 电气性能 | 体积固有抵抗 | ASTM D-257 | 1015 | Ω.m | |
| 诱电率力 | ASTM D-150-647 | 0.5 | |||
| 失电率 | ASTM D-150 | 0.19 | |||
| 诱电率 | ASTM D-150-647b | 3.7 | |||
| 燃烧率 | 1/16"HB | UL-94 | |||
| 绝缘耐力 | ASTM D-149 | 500 | Volts/Mil | ||
| 热性能 | 维卡软化点 | ASTM D-1525 | 105/221 | °C/°F | |
| 热变形温度 | ASTM D-648 | 92/198 | °C/°F | ||