| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 |
吸水率 | 24hr,23℃ | ASTM D-570 | 0.15 | % | |
| 平衡，23℃，相对湿度50% | ASTM D-570 | 0.32 | % | |||
| 密度 | ASTM D-792 | 1200 | kg/m3 | |||
| 熔体流动速率 | 300℃/1.2kg | ASTM D-1238 | 2.5 | g/10min | ||
| 收缩率 - 流动 | ASTM D955 | 0.50 到 0.70 | % | |||
| 物理性能 | 折射率 | ASTM D-542 | 1.586 | |||
| 透射率 | ASTM D1003 | 89.0 | % | |||
| 雾度 | ASTM D-1003 | 0.7-1.5 | % | |||
| 机械性能 | 伸长率 | 屈服点 | ASTM D-638 | 6.0 | % | |
| 断裂点 | ASTM D-638 | 150 | % | |||
| 悬壁梁缺口冲击强度 | 23℃ | ASTM D-256 | 950 | J/m | ||
| 无缺口悬臂梁冲击 | 23℃ | ASTM D-256 | 无断裂 | |||
| 装有测量仪表的落镖冲击 | 23℃, Total Energy | ASTM D3763 | 94 | J | ||
| 弯曲强度 | ASTM D-790 | 96 | MPa | |||
| 洛氏硬度 | M 计秤 | ASTM D-785 | 74 | M标度 | ||
| 洛氏硬度 | R 计秤 | ASTM D-785 | 118 | |||
| 弯曲模量 | ASTM D-790 | 2410 | MPa | |||
| 耐磨耗性 - Change in Haze | ASTM D1004 | 45 | % | |||
| 拉伸模量 | ASTM D-638 | 2410 | MPa | |||
| 抗张强度 | 屈服点 | ASTM D-638 | 60 | MPa | ||
| 断裂点 | ASTM D-638 | 72 | MPa | |||
| 电气性能 | 体积电阻率 | 23℃ ,干 | ASTM D-257 | 2.0×1017 | Ω.cm | |
| 漏电起痕指数 | 2mm | IEC 60112 | 250 | v | ||
| 介电强度 | ASTM D-149 | 3.00 | ||||
| 损耗因素 | 60Hz | ASTM D-150 | 0.001 | |||
| 介电常数 | 60Hz | ASTM D-150 | 17 | kv/mm | ||
| 热性能 | 球状压良温度 | IEC 598-1 | 125 | ℃ | ||
| 维卡软化点 | 50 C/hour | ASTM D-1525 | 151 | ℃ | ||
| 热变形温度 | 退火@1.8MPa(4 mm) | ASTM D-648 | 143 | ℃ | ||
| 线形膨胀系数 - 流动 | -40℃-82℃ | ASTM D-696 | 68×10-6 | mm/mm/℃ | ||
| 热变形温度 | 退火@0.45MPa(4 mm) | ASTM D-648 | 146 | ℃ | ||
| 热变形温度 | 未退火@1.8MPa(4 mm) | ASTM D-648 | 132 | ℃ | ||
| 其它性能 | 极限氧指数 | ASTM D-2863 | 26 | % | ||
| 平均燃烧程度 | ASTM D635 | 25 | mm | |||
| 热灯丝点火温度 | 2.00 mm | IEC 60695-2-13 | 850 | ℃ | ||