苏州天涛塑化有限公司
PP/7633
原料技术数据
| 性能项目 | 试验条件[状态] | 测试数据 | 测试数据 | 测试方法 | |
| 物理性能 | 比重 | 0.897 | g/cm3 | ASTM D792 | |
| 熔流率 | (230°C/2.16 kg) | 2 | g/10 min | ASTM D1238 | |
| 收缩率 | 流动 | 1.4 | % | ASTM D955 | |
| 洛氏硬度 | (R 计秤) | 81 | ASTM D785 | ||
| 机械性能 | 抗张强度 | (屈服) | 26 | MPa | ASTM D638 |
| 伸长率 | (屈服) | 8 | % | ASTM D638 | |
| 弯曲模量 | 1280 | MPa | ASTM D790 | ||
| 冲击性能 | 悬壁梁缺口冲击强度 | (23°C) | 180 | J/m | ASTM D256 |
| 无缺口悬臂梁冲击 | (-18°C) | 1300 | J/m | ASTM D256 | |
| Drop Impact Resistance | (-29°C) | 29.8 | J | Internal Method | |
| 热性能 | 热变形温度 | (0.45 MPa, 未退火) | 90 | °C | ASTM D648 |
| RTI Elec | UL 746 | ||||
| 1.50 mm | 115 | °C | |||
| 3.00 mm | 115 | °C | |||
| RTI Imp | UL 746 | ||||
| 1.50 mm | 115 | °C | |||
| 3.00 mm | 115 | °C | |||
| RTI Str | UL 746 | ||||
| 1.50 mm | 115 | °C | |||
| 3.00 mm | 115 | °C | |||
| 电气性能 | 耐电弧性 (1.50 mm) | PLC 5 | ASTM D495 | ||
| 相比耐漏电起痕指数(CTI) (1.50 mm) | PLC 1 | UL 746 | |||
| 高电弧燃烧指数(HAI) | UL 746 | ||||
| 1.50 mm | PLC 2 | ||||
| 3.00 mm | PLC 3 | ||||
| 高电压电弧起痕速率 (HVTR) (1.50 mm) | PLC 0 | UL 746 | |||
| 热丝引燃 (HWI) | UL 746 | ||||
| 1.50 mm | PLC 0 | ||||
| 3.00 mm | PLC 0 | ||||
| 可燃性 | UL 阻燃等级 | UL 94 | |||
| 1.50 mm, NC | HB | ||||
| 3.00 mm, ALL | HB |