基础创新食品级PPO SE1GFN2 20%玻纤增强 防火阻燃 耐水解 食品级PPO.
NORYL? SE1GFN2 resin
聚苯醚 + PS
20% 玻璃纤维增强材料
产品说明：
NORYL SE1GFN2 is a 20% glass reinforced, injection moldable modified polyphenylene ether resin. Designed for improved dimensional stability and good flow , this resin also uses non-chlorinated, non-brominated FR additives to achieve a V1 UL94 rating at 1.5 mm and UL94 5VA rating @ 2.0 mm. NORYL SE1GFN2 has a GWIT of 800C @ 1.00 mm according to IEC 60695-2-13. NORYL SE1GFN2 may be an excellent material candidate for electrical or electronic applications requiring good rheological properties, heat resistance, hydrolysis resistance, low density and thin wall flame resistance. SE1GFN2 is halogen free according to VDE/DIN 472 part 815.
NORYL? SE1GFN2 resin 物性表
| 基本信息 |
|
| 黄卡编号 |
|
| 填料/增强材料 |
|
| 添加剂 |
|
| 特性 |
- Chlorine Free
- 尺寸稳定性良好
- 低密度
- 良好的流动性
- 耐热性，中等
- 耐水解性
- 无溴
- 阻燃性
|
| 用途 |
|
| 机构评级 |
|
| RoHS 合规性 |
|
| 加工方法 |
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
1.25 |
g/cm3 |
ASTM D792, ISO 1183 |
| 溶化体积流率（MVR）(280°C/10.0 kg) |
12.0 |
cm3/10min |
ISO 1133 |
| 收缩率 - 流动1 |
0.20 到 0.40 |
% |
内部方法 |
| 吸水率 |
|
|
ISO 62 |
| 饱和, 23°C |
0.22 |
% |
ISO 62 |
| 平衡, 23°C, 50% RH |
0.070 |
% |
ISO 62 |
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 球压硬度(H 358/30) |
125 |
MPa |
ISO 2039-1 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量 |
5500 |
MPa |
ISO 527-2/1 |
| 拉伸应力(断裂) |
80.0 |
MPa |
ISO 527-2/5 |
| 拉伸应变(断裂) |
2.0 |
% |
ISO 527-2/5 |
| 弯曲模量2 |
4500 |
MPa |
ISO 178 |
| 弯曲应力 |
125 |
MPa |
ISO 178 |
| 泰伯耐磨性(1000 Cycles, 1000 g, CS-17 转轮) |
65.0 |
mg |
内部方法 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 简支梁无缺口冲击强度3 |
|
|
ISO 179/1eU |
| -30°C |
30 |
kJ/m2 |
ISO 179/1eU |
| 23°C |
30 |
kJ/m2 |
ISO 179/1eU |
| 无缺口伊佐德冲击强度4 |
|
|
ISO 180/1U |
| -30°C |
25 |
kJ/m2 |
ISO 180/1U |
| 23°C |
25 |
kJ/m2 |
ISO 180/1U |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 热变形温度5 |
|
|
|
| 0.45 MPa, 未退火, 100 mm 跨距 |
135 |
°C |
ISO 75-2/Be |
| 1.8 MPa, 未退火, 100 mm 跨距 |
130 |
°C |
ISO 75-2/Ae |
| 维卡软化温度 |
|
|
|
| -- |
150 |
°C |
ISO 306/A50 |
| -- |
140 |
°C |
ISO 306/B50 |
| -- |
145 |
°C |
ISO 306/B120 |
| Ball Pressure Test |
|
|
IEC 60695-10-2 |
| 125°C |
Pass |
|
IEC 60695-10-2 |
| 135°C6 |
Pass |
|
IEC 60695-10-2 |
| 线形热膨胀系数 |
|
|
|
| 流动 : -40 到 40°C |
5.0E-5 |
cm/cm/°C |
ASTM E831, ISO 11359-2 |
| 流动 : 23 到 80°C |
3.0E-5 |
cm/cm/°C |
ISO 11359-2 |
| 横向 : -40 到 40°C |
6.8E-5 |
cm/cm/°C |
ASTM E831, ISO 11359-2 |
| 横向 : 23 到 80°C |
7.0E-5 |
cm/cm/°C |
ISO 11359-2 |
| 导热系数 |
0.28 |
W/m/K |
ISO 8302 |
| RTI Elec |
110 |
°C |
UL 746 |
| RTI Imp |
105 |
°C |
UL 746 |
| RTI |
110 |
°C |
UL 746 |
| 电气性能 |
额定值 |
单位制 |
测试方法 |
| 表面电阻率 |
1.0E+15 |
ohms |
IEC 60093 |
| 体积电阻率 |
1.0E+15 |
ohms·cm |
IEC 60093 |
| 介电强度 |
|
|
IEC 60243-1 |
| 0.800 mm, 在油中 |
30 |
kV/mm |
IEC 60243-1 |
| 1.60 mm, 在油中 |
25 |
kV/mm |
IEC 60243-1 |
| 3.20 mm, 在油中 |
16 |
kV/mm |
IEC 60243-1 |
| 相对电容率 |
|
|
IEC 60250 |
| 50 Hz |
3.00 |
|
IEC 60250 |
| 60 Hz |
3.00 |
|
IEC 60250 |
| 1 MHz |
2.90 |
|
IEC 60250 |
| 耗散因数 |
|
|
IEC 60250 |
| 50 Hz |
4.0E-3 |
|
IEC 60250 |
| 60 Hz |
4.0E-3 |
|
IEC 60250 |
| 1 MHz |
2.0E-3 |
|
IEC 60250 |
| 相比耐漏电起痕指数(CTI) |
PLC 3 |
|
UL 746 |
| 漏电起痕指数 |
225 |
V |
IEC 60112 |
| 可燃性 |
额定值 |
单位制 |
测试方法 |
| UL 阻燃等级 |
|
|
UL 94 |
| 1.50 mm |
V-1 |
|
UL 94 |
| 6.00 mm |
V-0 |
|
UL 94 |
| 2.00 mm |
5VA |
|
UL 94 |
| 灼热丝易燃指数(3.20 mm) |
960 |
°C |
IEC 60695-2-12 |
| 热灯丝点火温度 |
|
|
IEC 60695-2-13 |
| 1.00 mm |
800 |
°C |
IEC 60695-2-13 |
| 2.00 mm |
800 |
°C |
IEC 60695-2-13 |
| 极限氧指数 |
30 |
% |
ISO 4589-2 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
100 到 120 |
°C |
|
| 干燥时间 |
2.0 到 3.0 |
hr |
|
| 料斗温度 |
60.0 到 80.0 |
°C |
|
| 料筒后部温度 |
240 到 260 |
°C |
|
| 料筒中部温度 |
260 到 280 |
°C |
|
| 料筒前部温度 |
280 到 300 |
°C |
|
| 射嘴温度 |
260 到 280 |
°C |
|
| 加工（熔体）温度 |
280 到 300 |
°C |
|
| 模具温度 |
80.0 到 120 |
°C |
|
| 备注 |
| 1 . |
Tensile Bar |
| 2 . |
2.0 mm/min |
| 3 . |
80*10*4 sp=62mm |
| 4 . |
80*10*4 |
| 5 . |
120*10*4 mm |
| 6 . |
Approximate maximum |