Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 06-002

POM copolymer

Extremely easy flowing Injection molding type for very thin-walled
precision molded parts with unfavourite flow-path-wallthickness
relation; permits processing at reduced temperature and also shorter
cycle times; for mechanical lower requirements; good chemical
resistance to solvents, fuel and strong alkalis as well as good
hydrolysis resistance; high resistance to thermal and oxidative
degradation.

Monomers and additives are listed in EU-Regulation (EU) 10/2011
FDA compliant according to 21 CFR 177.2470


UL-registration in natural a thickness more than 0.81 mm, in black a
thickness more than 1.5 mm as UL 94 HB, temperature index UL 746 B
for a thickness of 1.5 mm, electrical 105°C, mechanical 90°C

Burning rate ISO 3795 and FMVSS 302 75 mm/min for a thickness more
than 1 mm.

Ranges of applications: For very thin-walled precision molded parts
with unfavourite flow-path-wallthickness relation; permits
processing at reduced temperature and also shorter cycle times.

FDA = Food and Drug Administration (USA)
FMVSS = Federal Motor Vehicle Safety Standard (USA)

UL = Underwriters Laboratories (USA)

Hostaform? C 52021 物性表

基本信息
黄卡编号	E42337-234606 E42337-609721
特性	抗溶剂性 快的成型周期 流动性高 耐化学性良好 耐碱 耐燃油性 耐水解性
用途	薄壁部件
机构评级	FDA 21 CFR 177.2470 欧洲 10/1/2011 12:00:00 AM
RoHS 合规性	联系制造商
加工方法	注射成型
多点数据	Isothermal Stress vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Shear Stress vs. Shear Rate (ISO 11403-1)
树脂ID (ISO 1043)	POM

物理性能	额定值	单位制	测试方法
密度	1.41	g/cm3	ISO 1183
溶化体积流率（MVR）(190°C/2.16 kg)	39.0	cm3/10min	ISO 1133
收缩率			ISO 294-4
垂直流动方向	1.8	%	ISO 294-4
流动方向	1.9	%	ISO 294-4
吸水率(饱和, 23°C)	0.65	%	ISO 62

机械性能	额定值	单位制	测试方法
拉伸模量	3000	MPa	ISO 527-2/1A/1
拉伸应力(屈服)	65.0	MPa	ISO 527-2/1A/50
拉伸应变(屈服)	7.0	%	ISO 527-2/1A/50
标称拉伸断裂应变	15	%	ISO 527-2/1A/50
拉伸蠕变模量			ISO 899-1
1 hr	2500	MPa	ISO 899-1
1000 hr	1300	MPa	ISO 899-1
弯曲模量(23°C)	2800	MPa	ISO 178

冲击性能	额定值	单位制	测试方法
简支梁缺口冲击强度			ISO 179/1eA
-30°C	5.0	kJ/m2	ISO 179/1eA
23°C	5.0	kJ/m2	ISO 179/1eA
简支梁无缺口冲击强度			ISO 179/1eU
-30°C	100	kJ/m2	ISO 179/1eU
23°C	100	kJ/m2	ISO 179/1eU

热性能	额定值	单位制	测试方法
热变形温度(1.8 MPa, 未退火)	106	°C	ISO 75-2/A
熔融温度1	166	°C	ISO 11357-3
线形热膨胀系数 - 流动	1.1E-4	cm/cm/°C	ISO 11359-2

电气性能	额定值	单位制	测试方法
表面电阻率	1.0E 14	ohms	IEC 60093
体积电阻率	1.0E 14	ohms·cm	IEC 60093
介电强度	35	kV/mm	IEC 60243-1
相对电容率			IEC 60250
100 Hz	4.00		IEC 60250
1 MHz	4.00		IEC 60250
耗散因数			IEC 60250
100 Hz	3.0E-3		IEC 60250
1 MHz	5.0E-3		IEC 60250
漏电起痕指数	600	V	IEC 60112

可燃性	额定值	单位制	测试方法
UL 阻燃等级			UL 94
0.810 mm	HB		UL 94
1.50 mm	HB		UL 94

充模分析	额定值	单位制	测试方法
Density of Melt	1.200	g/cm3	内部方法
Ejection Temperature	163	°C	内部方法
Specific Heat Capacity of Melt	2060	J/kg/°C	内部方法
Thermal Conductivity of Melt	0.19	W/m/K	内部方法

注射	额定值	单位制
干燥温度	120 到 140	°C
干燥时间	3.0 到 4.0	hr
建议的最大水分含量	0.15	%
料斗温度	20.0 到 30.0	°C
料筒后部温度	170 到 180	°C
料筒中部温度	180 到 190	°C
料筒前部温度	190 到 200	°C
射嘴温度	190 到 210	°C
加工（熔体）温度	190 到 210	°C
模具温度	80.0 到 120	°C
注塑压力	60.0 到 120	MPa
注射速度	慢到中等
保压	60.0 到 120	MPa
背压	0.00 到 4.00	MPa

注射说明
Manifold Temperature: 190 to 210°CZone 4 Temperature: 190 to 210°CFeed Temperature: 60 to 80°C

备注
1 .	10°C/min