PETG 韩国SK K2012 聚对苯二甲酸乙二醇酯 PETG材料
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
1.27 |
g/cm3 |
ASTM 792 |
| 吸水率(24 hr) |
0.20 |
% |
ASTM 570 |
| Color b - Hunter1 |
|
|
ASTM E308 |
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 洛氏硬度(R 级) |
116 |
|
ASTM 785 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 抗张强度 |
|
|
ASTM 638 |
| 屈服 |
53.0 |
MPa |
ASTM 638 |
| 断裂 |
26.0 |
MPa |
ASTM 638 |
| 伸长率2 |
|
|
ASTM 638 |
| 屈服 |
5.0 |
% |
ASTM 638 |
| 断裂 |
70 |
% |
ASTM 638 |
| 弯曲模量 |
2150 |
MPa |
ASTM 790 |
| 弯曲强度3 |
80.0 |
MPa |
ASTM 790 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 悬壁梁缺口冲击强度(23°C) |
90 |
J/m |
ASTM 256 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
ASTM 648 |
| 0.45 MPa, 未退火 |
74.0 |
°C |
ASTM 648 |
| 1.8 MPa, 未退火 |
70.0 |
°C |
ASTM 648 |
| 维卡软化温度 |
83.0 |
°C |
ASTM 15254 |
| 电气性能 |
额定值 |
单位制 |
测试方法 |
| 表面电阻率 |
1.0E+16 |
ohms |
ASTM 257 |
| 体积电阻率 |
1.0E+15 |
ohms·cm |
ASTM 257 |
| 介电强度5 |
16 |
kV/mm |
ASTM 149 |
| 介电常数 |
|
|
ASTM 150 |
| 1 kHz |
2.60 |
|
ASTM 150 |
| 1 MHz |
2.40 |
|
ASTM 150 |
| 耗散因数 |
|
|
ASTM 150 |
| 1 kHz |
5.0E-3 |
|
ASTM 150 |
| 1 MHz |
0.023 |
|
ASTM 150 |
| 可燃性 |
额定值 |
单位制 |
测试方法 |
| UL 阻燃等级 |
|
|
UL 94 |
| 1.00 mm |
HB |
|
UL 94 |
| 1.50 mm |
HB |
|
UL 94 |
| 3.00 mm |
V-2 |
|
UL 94 |