TPEE KEYFLEX BT 1245D
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.13g/cc | 1.13g/cc | ASTM D792 |
Water Absorption | 0.60 % @Temperature 23.0 °C, Time 86400 sec |
0.60 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
Linear Mold Shrinkage, Flow | 0.014-0.018cm/cm @Thickness 3.20 mm |
0.014-0.018in/in @Thickness 0.126 in |
ASTM D955 |
Melt Flow | 25g/10 min @Load 2.16 kg, Temperature 220 °C |
25g/10 min @Load 4.76 lb, Temperature 428 °F |
ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Hardness, Shore D | 44 | 44 | ASTM D2240 |
Tensile Strength at Break | 29.1MPa @Thickness 2.00 mm |
4220psi @Thickness 0.0787 in |
50mm/min; ASTM D638 |
Elongation at Break | 600 % @Thickness 2.00 mm |
600 % @Thickness 0.0787 in |
50mm/min; ASTM D638 |
TPEE KEYFLEX BT 1245D
TPEE它是一种酯体系热塑性弹性体(Thermoplastic elastomers),其柔软性与弹性恢复力酷似橡胶,而机械性强度、耐热性及耐候性方面比橡胶优秀。不经过硫化工程,与普通热塑性树脂相同,以易于成型加工的树脂根据通常聚酯合成方法妥当调整软链段的共聚物量,从而形成适合各种用途的柔软性与机械性材质。
特性:
⒈良好的抗蠕变,抗冲击和抗疲劳性能。
⒉高冲击强度和良好的低温柔韧性。
⒊温度上升时保持良好的性能。
⒋良好的对化学物质,油品,溶剂和天气的抵抗能力。
⒌高抗撕裂强度及高耐摩擦性能。
⒍易加工且具经济性。
⒎良好的可回收性。
TPEE应用
TPEE主要用于要求减震、耐冲击、耐曲挠、密封性和弹性、耐油、耐化学品并要求足够强度的领域。如:聚合物改性、汽车部件、耐高低温电线护套、液压软管、鞋材、传动皮带、旋转成型轮胎、挠性连轴节、消音齿轮、电梯滑道、化工设备管道阀件中的防腐耐磨耐高低温材料等。TPEE高性能的产品牌号有美国杜邦公司的TPEE 5526,5556,4056,4069等,广泛用于电线电缆以及密封件等。
1天线
其优异的耐外部环境,耐臭氧,耐紫外线,耐侯性,可以减少信号接收损失,优异的手感是汽车天线和手机天线的最佳选择。
2发动机进气管
加工进气管的方法通常采用3-D或负压式吹塑,这是一种用相对简单而且低成本的模具来制作较长的中空管的成型技术。方便简单的安装和加工工艺使得TPEE在这一零部件的生产中得到广泛应用。吹塑成型可以减少部件的数量和安装的流程,从而使部件成本小于传统橡胶方案。
TPEE KEYFLEX BT 1245D我司所销售所有产品均为原厂原包,均可提供相关资料报告(如:物性表,MSDS报告,UL报告,COA报告,SGS报告,FDA等)!