Ultramid? A3EG10 | PA66-GF50 | BASF
Product Texts
A Glass fibre reinforced injection moulding grade for industrial parts requiring high rigidity and providing electrical insulation.
| Rheological properties |
dry / cond |
Unit |
Test Standard |
| Melt volume-flow rate, MVR |
8 / * |
cm3/10min |
ISO 1133 |
| Temperature |
275 / * |
°C |
ISO 1133 |
| Load |
5 / * |
kg |
ISO 1133 |
| Molding shrinkage, parallel |
0.3 / * |
% |
ISO 294-4, 2577 |
| Molding shrinkage, normal |
0.8 / * |
% |
ISO 294-4, 2577 |
| Mechanical properties |
dry / cond |
Unit |
Test Standard |
| Tensile modulus |
16800 / 12500 |
MPa |
ISO 527-1/-2 |
| Stress at break |
240 / 180 |
MPa |
ISO 527-1/-2 |
| Strain at break |
2.5 / 3.5 |
% |
ISO 527-1/-2 |
| Tensile creep modulus, 1h |
* / 9800 |
MPa |
ISO 899-1 |
| Tensile creep modulus, 1000h |
* / 7800 |
MPa |
ISO 899-1 |
| Charpy impact strength,23°C |
95 / 100 |
kJ/m2 |
ISO 179/1eU |
| Charpy impact strength, -30°C |
90 / - |
kJ/m2 |
ISO 179/1eU |
| Charpy notched impact strength,23°C |
18 / 25 |
kJ/m2 |
ISO 179/1eA |
| Charpy notched impact strength, -30°C |
13 / - |
kJ/m2 |
ISO 179/1eA |
| Thermal properties |
dry / cond |
Unit |
Test Standard |
| Melting temperature, 10°C/min |
260 / * |
°C |
ISO 11357-1/-3 |
| Temp. of deflection under load, 1.80 MPa |
250 / * |
°C |
ISO 75-1/-2 |
| Temp. of deflection under load, 0.45 MPa |
260 / * |
°C |
ISO 75-1/-2 |
| Vicat softening temperature, 50°C/h 50N |
250 / * |
°C |
ISO 306 |
| Coeff. of linear therm. expansion, parallel |
16 / * |
E-6/K |
ISO 11359-1/-2 |
| Coeff. of linear therm. expansion, normal |
80 / * |
E-6/K |
ISO 11359-1/-2 |
| Burning Behav. at 1.5 mm nom. thickn. |
HB / * |
class |
IEC 60695-11-10 |
| Thickness tested (1.5) |
1.5 / * |
mm |
IEC 60695-11-10 |
| Yellow Card available |
Yes / * |
- |
- |
| Burning Behav. at thickness h |
HB / * |
class |
IEC 60695-11-10 |
| Thickness tested (h) |
0.8 / * |
mm |
IEC 60695-11-10 |
| Yellow Card available |
Yes / * |
- |
- |
| Electrical properties |
dry / cond |
Unit |
Test Standard |
| Relative permittivity, 1MHz |
3.8 / 6.6 |
- |
IEC 62631-2-1 |
| Dissipation factor, 100Hz |
150 / 1700 |
E-4 |
IEC 62631-2-1 |
| Dissipation factor, 1MHz |
150 / 1700 |
E-4 |
IEC 62631-2-1 |
| Volume resistivity |
1E13 / 1E10 |
Ohm*m |
IEC 62631-3-1 |
| Surface resistivity |
* / 1E10 |
Ohm |
IEC 62631-3-2 |
| Electric strength |
40 / 37 |
kV/mm |
IEC 60243-1 |
| Comparative tracking index |
- / 550 |
- |
IEC 60112 |
| Other properties |
dry / cond |
Unit |
Test Standard |
| Water absorption |
4 / * |
% |
Sim. to ISO 62 |
| Humidity absorption |
1.2 / * |
% |
Sim. to ISO 62 |
| Density |
1560 / - |
kg/m3 |
ISO 1183 |
| Material specific properties |
dry / cond |
Unit |
Test Standard |
| Viscosity number |
130 / * |
cm3/g |
ISO 307, 1157, 1628 |
| Rheological calculation properties |
Value |
Unit |
Test Standard |
| Density of melt |
1340 |
kg/m3 |
- |
| Spec. heat capacity melt |
1950 |
J/(kg K) |
- |
| Ejection temperature |
200 |
°C |
- |
| Test specimen production |
Value |
Unit |
Test Standard |
| Injection Molding, melt temperature |
300 |
°C |
ISO 294 |
| Injection Molding, mold temperature |
80 |
°C |
ISO 294 |
| Injection Molding, injection velocity |
200 |
mm/s |
ISO 294 |