上海沐音新材料有限公司
LEXAN? VR2020 resin
聚碳酸酯
产品说明:
Mid-flow, UV stabilized polycarbonate resin with mold release. Available in limited transparent tints, limited package types, and must meet minimum order quantity requirements.
| 总体 | |
|
材料状态
|
|
|
资料1
|
|
|
UL 黄卡2
|
|
|
搜索 UL 黄卡
|
SABIC Innovative PlasticsLEXAN? |
|
供货地区
|
|
|
添加剂
|
脱模紫外线稳定剂 |
|
特性
|
抗紫外线性能良好流动性中等 |
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
|||
|
--
|
1.20
|
g/cm3
|
ASTM D792,ISO 1183 |
|
--
|
1.19
|
g/cm3
|
ASTM D792 |
|
特定体积
|
0.830
|
cm3/g
|
ASTM D792 |
|
熔流率（熔体流动速率）(300°C/1.2 kg)
|
18
|
g/10 min
|
ASTM D1238 |
|
溶化体积流率（MVR）(220°C/5.0 kg)
|
21.0
|
cm3/10min
|
ISO 1133 |
|
收缩率 - 流动(3.20 mm)
|
0.50 到 0.70
|
%
|
内部方法 |
|
吸水率
|
|||
|
24 hr
|
0.15
|
%
|
ASTM D570 |
|
饱和, 23°C
|
0.35
|
%
|
ISO 62 |
|
平衡, 23°C
|
0.35
|
%
|
ASTM D570 |
|
平衡, 100°C
|
0.58
|
%
|
ASTM D570 |
|
平衡, 23°C, 50% RH
|
0.15
|
%
|
ISO 62 |
|
室外适用性
|
f1
|
|
UL 746C |
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
洛氏硬度
|
ASTM D785 | ||
|
M 级
|
70
|
|
|
|
R 级
|
118
|
|
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
--3
|
2380
|
MPa
|
ASTM D638 |
|
--
|
2350
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服4
|
62.1
|
MPa
|
ASTM D638 |
|
屈服
|
63.0
|
MPa
|
ISO 527-2/50 |
|
断裂4
|
65.5
|
MPa
|
ASTM D638 |
|
断裂
|
65.0
|
MPa
|
ISO 527-2/50 |
|
伸长率
|
|||
|
屈服4
|
7.0
|
%
|
ASTM D638 |
|
屈服
|
6.0
|
%
|
ISO 527-2/50 |
|
断裂4
|
110
|
%
|
ASTM D638 |
|
断裂
|
100
|
%
|
ISO 527-2/50 |
|
弯曲模量
|
|||
|
50.0 mm 跨距5
|
2340
|
MPa
|
ASTM D790 |
|
--6
|
2300
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
--6,7
|
90.0
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距5
|
93.1
|
MPa
|
ASTM D790 |
|
泰伯耐磨性(1000 Cycles, 1000 g, CS-17 转轮)
|
10.0
|
mg
|
ASTM D1044 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁无缺口冲击强度8(23°C)
|
无断裂
|
|
ISO 179/1eU |
|
悬壁梁缺口冲击强度
|
|||
|
23°C
|
690
|
J/m
|
ASTM D256 |
|
-30°C9
|
10
|
kJ/m2
|
ISO 180/1A |
|
23°C9
|
12
|
kJ/m2
|
ISO 180/1A |
|
无缺口悬臂梁冲击(23°C)
|
3200
|
J/m
|
ASTM D4812 |
|
落锤冲击(23°C)
|
169
|
J
|
ASTM D3029 |
|
拉伸冲击强度10
|
546
|
kJ/m2
|
ASTM D1822 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
0.45 MPa, 未退火, 6.40 mm
|
138
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 6.40 mm
|
132
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 100 mm 跨距11
|
122
|
°C
|
ISO 75-2/Ae |
|
维卡软化温度
|
|||
|
--
|
154
|
°C
|
ASTM D152512 |
|
--
|
140
|
°C
|
ISO 306/B50 |
|
--
|
141
|
°C
|
ISO 306/B120 |
|
Ball Pressure Test
|
IEC 60695-10-2 | ||
|
125°C
|
Pass
|
|
|
|
140°C13
|
Pass
|
|
|
|
线形热膨胀系数
|
|||
|
流动 : -40 到 95°C
|
6.8E-5
|
cm/cm/°C
|
ASTM E831 |
|
流动 : 23 到 80°C
|
7.0E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
横向 : 23 到 80°C
|
7.0E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
比热
|
1260
|
J/kg/°C
|
ASTM C351 |
|
导热系数
|
0.19
|
W/m/K
|
ASTM C177 |
|
RTI Elec
|
100
|
°C
|
UL 746 |
|
RTI Imp
|
100
|
°C
|
UL 746 |
|
RTI
|
100
|
°C
|
UL 746 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
体积电阻率
|
1.0E 17
|
ohm·cm
|
ASTM D257 |
|
介电强度(3.20 mm, in Air)
|
15
|
kV/mm
|
ASTM D149 |
|
介电常数
|
ASTM D150 | ||
|
50 Hz
|
3.17
|
|
|
|
60 Hz
|
3.17
|
|
|
|
1 MHz
|
2.96
|
|
|
|
耗散因数
|
ASTM D150 | ||
|
50 Hz
|
9.0E-4
|
|
|
|
60 Hz
|
9.0E-4
|
|
|
|
1 MHz
|
0.010
|
|
|
|
相比耐漏电起痕指数(CTI)
|
PLC 2
|
|
UL 746 |
|
高电弧燃烧指数(HAI)
|
PLC 1
|
|
UL 746 |
|
高电压电弧起痕速率 (HVTR)
|
PLC 2
|
|
UL 746 |
|
热丝引燃 (HWI)
|
PLC 4
|
|
UL 746 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级(0.760 mm)
|
HB
|
|
UL 94 |
| 光学性能 |
额定值
|
单位制
|
测试方法
|
|
折射率
|
1.586
|
|
ASTM D542 |
|
透射率(2540 μm)
|
88.0
|
%
|
ASTM D1003 |
|
雾度(2540 μm)
|
1.0
|
%
|
ASTM D1003 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
121
|
°C
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
干燥时间，最大
|
48
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 60
|
%
|
|
|
料筒后部温度
|
260 到 282
|
°C
|
|
|
料筒中部温度
|
271 到 293
|
°C
|
|
|
料筒前部温度
|
282 到 304
|
°C
|
|
|
射嘴温度
|
277 到 299
|
°C
|
|
|
加工（熔体）温度
|
282 到 304
|
°C
|
|
|
模具温度
|
71.1 到 93.3
|
°C
|
|
|
背压
|
0.345 到 0.689
|
MPa
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
0.025 到 0.076
|
mm
|
| 备注 |
 |