上海沐音新材料有限公司
LEXAN? VR1820 resin
聚碳酸酯
产品说明:
VR1820 resin is a high flow (MFR = 22 at 300°C/1.2kg), heat and UV stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.
| 总体 | ||||
|
材料状态
|
|
|||
|
资料1
|
||||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
添加剂
|
|
|||
|
特性
|
|
|||
|
RoHS 合规性
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.20
|
g/cm3
|
ASTM D792,ISO 1183 |
|
熔流率（熔体流动速率）(300°C/1.2 kg)
|
22
|
g/10 min
|
ASTM D1238 |
|
溶化体积流率（MVR）(300°C/1.2 kg)
|
21.0
|
cm3/10min
|
ISO 1133 |
|
收缩率 - 流动
|
内部方法 | ||
|
--2
|
0.50 到 0.70
|
%
|
|
|
3.20 mm
|
0.50 到 0.70
|
%
|
|
|
吸水率
|
|||
|
饱和, 23°C
|
0.35
|
%
|
ISO 62 |
|
平衡, 23°C
|
0.35
|
%
|
ASTM D570 |
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
洛氏硬度
|
|||
|
R 级
|
120
|
|
ASTM D785 |
|
R 计秤
|
120
|
|
ISO 2039-2 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
--3
|
2350
|
MPa
|
ASTM D638 |
|
--
|
2350
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服4
|
63.0
|
MPa
|
ASTM D638 |
|
屈服
|
63.0
|
MPa
|
ISO 527-2/50 |
|
伸长率
|
|||
|
屈服4
|
6.0
|
%
|
ASTM D638 |
|
屈服
|
6.0
|
%
|
ISO 527-2/50 |
|
断裂4
|
70
|
%
|
ASTM D638 |
|
断裂
|
70
|
%
|
ISO 527-2/50 |
|
弯曲模量
|
|||
|
50.0 mm 跨距5
|
2300
|
MPa
|
ASTM D790 |
|
--6
|
2300
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
--6,7
|
90.0
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距5
|
90.0
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度
|
|||
|
23°C
|
640
|
J/m
|
ASTM D256 |
|
-30°C8
|
12
|
kJ/m2
|
ISO 180/1A |
|
23°C8
|
65
|
kJ/m2
|
ISO 180/1A |
|
无缺口悬臂梁冲击
|
|||
|
23°C
|
无断裂
|
|
ASTM D4812,ISO 180/1U |
|
-30°C8
|
无断裂
|
|
ISO 180/1U |
|
装有测量仪表的落镖冲击(23°C, Energy at Peak Load)
|
55.0
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
0.45 MPa, 未退火, 3.20 mm
|
133
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 64.0 mm 跨距9
|
133
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, 未退火, 3.20 mm
|
122
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 64.0 mm 跨距9
|
122
|
°C
|
ISO 75-2/Af |
|
维卡软化温度
|
140
|
°C
|
ISO 306/B50,ASTM D152510 |
|
Ball Pressure Test(125°C)
|
Pass
|
|
IEC 60695-10-2 |
|
线形热膨胀系数 - 流动
|
|||
|
-40 到 95°C
|
7.0E-5
|
cm/cm/°C
|
ASTM E831 |
|
23 到 80°C
|
7.0E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
导热系数
|
0.20
|
W/m/K
|
ASTM C177,ISO 8302 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
体积电阻率
|
1.0E+15
|
ohm·cm
|
ASTM D257,IEC 60093 |
|
介电强度(1.60 mm)
|
27
|
kV/mm
|
ASTM D149,IEC 60243-1 |
|
介电常数
|
ASTM D150,IEC 60250 | ||
|
60 Hz
|
3.00
|
|
|
|
1 MHz
|
3.00
|
|
|
|
耗散因数
|
ASTM D150,IEC 60250 | ||
|
60 Hz
|
1.0E-3
|
|
|
|
1 MHz
|
0.010
|
|
| 光学性能 |
额定值
|
单位制
|
测试方法
|
|
折射率
|
1.586
|
|
ASTM D542,ISO 489 |
|
透射率(2540 μm)
|
88.0 到 90.0
|
%
|
ASTM D1003 |
|
雾度(2540 μm)
|
0.80
|
%
|
ASTM D1003 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
120
|
°C
|
|
|
干燥时间
|
2.0 到 4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
料斗温度
|
60.0 到 80.0
|
°C
|
|
|
料筒后部温度
|
260 到 280
|
°C
|
|
|
料筒中部温度
|
270 到 290
|
°C
|
|
|
料筒前部温度
|
280 到 300
|
°C
|
|
|
射嘴温度
|
270 到 290
|
°C
|
|
|
加工（熔体）温度
|
280 到 300
|
°C
|
|
|
模具温度
|
80.0 到 100
|
°C
|
| 备注 |
 |