LEXAN? ML6411 resin
聚碳酸酯
产品说明:
LEXAN ML6411 polycarbonate (PC) siloxane resin, is a high flow opaque injection molding (IM) grade with very low temperature ductility characteristics. This grade offers UL94 V0 @ 1.5mm and 5VA @ 3.0mm flame retardancy based on non-chlorine, non-bromine FR systems. LEXAN ML6411 resin offers excellent processing characteristics with opportunity for shorter IM cycle times compared to standard PC. This product is available in a wide range of opaque colors and is an excellent candidate for a wide range of electrical applications.
| 总体 | ||||
|
材料状态
|
|
|||
|
资料1
|
||||
|
UL 黄卡2
|
||||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
添加剂
|
|
|||
|
特性
|
|
|||
|
用途
|
|
|||
|
外观
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
|||
|
--
|
1.19
|
g/cm3
|
ASTM D792 |
|
--
|
1.20
|
g/cm3
|
ISO 1183 |
|
熔流率（熔体流动速率）(260°C/2.16 kg)
|
7.0
|
g/10 min
|
ASTM D1238 |
|
溶化体积流率（MVR）(260°C/5.0 kg)
|
18.0
|
cm3/10min
|
ISO 1133 |
|
收缩率 - 流动(3.20 mm)
|
0.40 到 0.80
|
%
|
内部方法 |
|
吸水率
|
ISO 62 | ||
|
饱和, 23°C
|
0.30
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.10
|
%
|
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
--3
|
2500
|
MPa
|
ASTM D638 |
|
--
|
2350
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服4
|
62.0
|
MPa
|
ASTM D638 |
|
屈服
|
62.0
|
MPa
|
ISO 527-2/50 |
|
断裂4
|
54.0
|
MPa
|
ASTM D638 |
|
断裂
|
58.0
|
MPa
|
ISO 527-2/50 |
|
伸长率
|
|||
|
屈服4
|
5.0
|
%
|
ASTM D638 |
|
屈服
|
5.0
|
%
|
ISO 527-2/50 |
|
断裂4
|
100
|
%
|
ASTM D638 |
|
断裂
|
100
|
%
|
ISO 527-2/50 |
|
弯曲模量
|
|||
|
50.0 mm 跨距5
|
2600
|
MPa
|
ASTM D790 |
|
--6
|
2350
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
--6,7
|
90.0
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距5
|
95.0
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度
|
|||
|
-30°C
|
150
|
J/m
|
ASTM D256 |
|
23°C
|
900
|
J/m
|
ASTM D256 |
|
-30°C8
|
15
|
kJ/m2
|
ISO 180/1A |
|
23°C8
|
60
|
kJ/m2
|
ISO 180/1A |
|
装有测量仪表的落镖冲击(23°C, Total Energy)
|
72.0
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
0.45 MPa, 未退火, 6.40 mm
|
128
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 100 mm 跨距9
|
125
|
°C
|
ISO 75-2/Be |
|
1.8 MPa, 未退火, 3.20 mm
|
114
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 6.40 mm
|
119
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 100 mm 跨距9
|
115
|
°C
|
ISO 75-2/Ae |
|
维卡软化温度
|
|||
|
--
|
134
|
°C
|
ASTM D152510,ISO 306/B5010 |
|
--
|
135
|
°C
|
ISO 306/B120 |
|
Ball Pressure Test(125°C)
|
Pass
|
|
IEC 60695-10-2 |
|
线形热膨胀系数
|
|||
|
流动 : -40 到 40°C
|
7.7E-5
|
cm/cm/°C
|
ASTM E831 |
|
流动 : -40 到 40°C
|
7.0E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
横向 : -40 到 40°C
|
5.9E-5
|
cm/cm/°C
|
ASTM E831 |
|
横向 : -40 到 40°C
|
7.0E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
RTI Elec
|
100
|
°C
|
UL 746 |
|
RTI Imp
|
100
|
°C
|
UL 746 |
|
RTI
|
100
|
°C
|
UL 746 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
体积电阻率
|
1.0E+15
|
ohm·cm
|
IEC 60093 |
|
介电强度(3.20 mm, in Oil)
|
27
|
kV/mm
|
ASTM D149 |
|
相比耐漏电起痕指数(CTI)
|
PLC 2
|
|
UL 746 |
|
漏电起痕指数
|
250
|
V
|
IEC 60112 |
|
高电弧燃烧指数(HAI)
|
PLC 1
|
|
UL 746 |
|
热丝引燃 (HWI)
|
PLC 3
|
|
UL 746 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级
|
UL 94 | ||
|
1.50 mm
|
V-0
|
|
|
|
2.00 mm
|
5VB
|
|
|
|
3.00 mm
|
5VA
|
|
|
|
3.00 mm, Testing by SABIC
|
5VA
|
|
|
|
灼热丝易燃指数(1.00 mm)
|
960
|
°C
|
IEC 60695-2-12 |
|
热灯丝点火温度
|
IEC 60695-2-13 | ||
|
1.00 mm
|
800
|
°C
|
|
|
2.00 mm
|
800
|
°C
|
|
|
3.00 mm
|
800
|
°C
|
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
90.0 到 100
|
°C
|
|
|
干燥时间
|
2.0 到 4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
料斗温度
|
60.0 到 80.0
|
°C
|
|
|
料筒后部温度
|
230 到 260
|
°C
|
|
|
料筒中部温度
|
250 到 290
|
°C
|
|
|
料筒前部温度
|
260 到 300
|
°C
|
|
|
射嘴温度
|
250 到 290
|
°C
|
|
|
加工（熔体）温度
|
270 到 300
|
°C
|
|
|
模具温度
|
60.0 到 90.0
|
°C
|
| 备注 |
  |