LEXAN? LUX9130C resin
聚碳酸酯
产品说明:
Lexan* LUX9130C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm, high flow capability and is UV stabilized providing additional weathering capability. Lexan* LUX9130C is available in clear transparent and tinted color options that is an excellent candidate for a wide variety of applications.
| 总体 | ||||
|
材料状态
|
|
|||
|
资料1
|
||||
|
UL 黄卡2
|
||||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
添加剂
|
|
|||
|
特性
|
|
|||
|
外观
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
|||
|
--
|
1.19
|
g/cm3
|
ASTM D792 |
|
--
|
1.20
|
g/cm3
|
ISO 1183 |
|
熔流率（熔体流动速率）(300°C/1.2 kg)
|
18
|
g/10 min
|
ASTM D1238 |
|
溶化体积流率（MVR）(300°C/1.2 kg)
|
17.0
|
cm3/10min
|
ISO 1133 |
|
收缩率
|
内部方法 | ||
|
流动 : 3.20 mm
|
0.55 到 0.75
|
%
|
|
|
横向流动 : 3.20 mm
|
0.60 到 0.80
|
%
|
|
|
吸水率
|
ISO 62 | ||
|
饱和, 23°C
|
0.13
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.11
|
%
|
|
|
室外适用性
|
f1
|
|
UL 746C |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
--3
|
2400
|
MPa
|
ASTM D638 |
|
--
|
2300
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服4
|
67.0
|
MPa
|
ASTM D638 |
|
屈服
|
63.0
|
MPa
|
ISO 527-2/50 |
|
断裂4
|
54.0
|
MPa
|
ASTM D638 |
|
断裂
|
57.0
|
MPa
|
ISO 527-2/50 |
|
伸长率
|
|||
|
屈服4
|
6.0
|
%
|
ASTM D638 |
|
屈服
|
6.0
|
%
|
ISO 527-2/50 |
|
断裂4
|
80
|
%
|
ASTM D638 |
|
断裂
|
73
|
%
|
ISO 527-2/50 |
|
弯曲模量
|
|||
|
50.0 mm 跨距5
|
2400
|
MPa
|
ASTM D790 |
|
--6
|
2400
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
--6,7
|
96.0
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距5
|
103
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度8
|
ISO 179/1eA | ||
|
-30°C
|
9.0
|
kJ/m2
|
|
|
23°C
|
10
|
kJ/m2
|
|
|
简支梁无缺口冲击强度8
|
ISO 179/1eU | ||
|
-30°C
|
无断裂
|
|
|
|
23°C
|
无断裂
|
|
|
|
悬壁梁缺口冲击强度
|
|||
|
-30°C
|
85
|
J/m
|
ASTM D256 |
|
23°C
|
100
|
J/m
|
ASTM D256 |
|
-30°C9
|
9.0
|
kJ/m2
|
ISO 180/1A |
|
23°C9
|
10
|
kJ/m2
|
ISO 180/1A |
|
无缺口悬臂梁冲击
|
ASTM D4812,ISO 180/1U | ||
|
-30°C
|
无断裂
|
|
|
|
23°C
|
无断裂
|
|
|
|
装有测量仪表的落镖冲击(23°C, Total Energy)
|
65.0
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
0.45 MPa, 未退火, 3.20 mm
|
130
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 100 mm 跨距10
|
131
|
°C
|
ISO 75-2/Be |
|
1.8 MPa, 未退火, 3.20 mm
|
120
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 100 mm 跨距10
|
121
|
°C
|
ISO 75-2/Ae |
|
维卡软化温度
|
|||
|
--
|
136
|
°C
|
ASTM D152511 |
|
--
|
139
|
°C
|
ISO 306/B50 |
|
--
|
140
|
°C
|
ISO 306/B120 |
|
Ball Pressure Test(125°C)
|
Pass
|
|
IEC 60695-10-2 |
|
线形热膨胀系数
|
|||
|
流动 : -40 到 40°C
|
6.8E-5
|
cm/cm/°C
|
ASTM E831 |
|
流动 : 23 到 80°C
|
7.7E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
横向 : -40 到 40°C
|
7.0E-5
|
cm/cm/°C
|
ASTM E831 |
|
横向 : 23 到 80°C
|
8.0E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
RTI Elec
|
130
|
°C
|
UL 746 |
|
RTI Imp
|
120
|
°C
|
UL 746 |
|
RTI
|
130
|
°C
|
UL 746 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
介电常数(1.10 GHz)
|
2.78
|
|
ASTM ES7-83 |
|
耗散因数(1.10 GHz)
|
5.6E-3
|
|
ASTM ES7-83 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级
|
UL 94 | ||
|
0.400 mm
|
V-2
|
|
|
|
1.50 mm
|
V-0
|
|
|
|
灼热丝易燃指数(1.50 mm)
|
960
|
°C
|
IEC 60695-2-12 |
|
热灯丝点火温度(1.50 mm)
|
850
|
°C
|
IEC 60695-2-13 |
| 光学性能 |
额定值
|
单位制
|
测试方法
|
|
透射率(2540 μm)
|
91.0
|
%
|
ASTM D1003 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
121
|
°C
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
干燥时间，最大
|
48
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 60
|
%
|
|
|
料筒后部温度
|
260 到 282
|
°C
|
|
|
料筒中部温度
|
271 到 293
|
°C
|
|
|
料筒前部温度
|
282 到 304
|
°C
|
|
|
射嘴温度
|
277 到 299
|
°C
|
|
|
加工（熔体）温度
|
282 到 304
|
°C
|
|
|
模具温度
|
71.1 到 93.3
|
°C
|
|
|
背压
|
0.345 到 0.689
|
MPa
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
0.025 到 0.076
|
mm
|
| 备注 |
  |