东莞市铭汇塑胶有限公司
LG Chemical MB885 Transparent impact modifier
Other Engineering Material,Additive/Filler for Polymer
LG Chemical
产品说明:
Description: MBS type transparent impact modifiers from LG Chemical is used to improve impact strength and processability of PVC products, and classified into transparent grade and low chlorosis grade by applications.
Application: Transparent sheet, film etc
Information provided by LG Chemical
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
比重 | 1.06 g/cc | 1.06 g/cc | |
体积密度 | = 0.320 g/cc | = 0.0116 lb/in3 | Aerated; LSY-QB-KD019 |
挥发物 | = 1.0 % | = 1.0 % | ISO 1625 |
粒子网格尺寸 | 20 Mesh | 20 Mesh | 3%, (mesh on); LSY-QB-KD028 |
200 Mesh | 200 Mesh | 20%, (mesh pass); LSY-QB-KD029 |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
Izod Impact, Unnotched | = 7.85 J/cm
@Temperature 23.0 °C
|
= 14.7 ft-lb/in
@Temperature 73.4 °F
|
ISO 180 |
= 7.85 J/cm
@Temperature 0.000 °C
|
= 14.7 ft-lb/in
@Temperature 32.0 °F
|
ISO 180 | |
冲击 | = 70 | = 70 | Rotary; LSY-QB-KD023 |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
熔融温度 | 132 - 149 °C | 270 - 300 °F | |
Flash Point | 400 °C | 752 °F |
光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
雾度 | = 16 % | = 16 % | LSY-QB-KD016 |
Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
材料描述 | 测试方法 | |
---|---|---|
Dynamic thermal stability | 15 | LSY-QB-KD007 |
Foreign Material | 3 (10 x 10 cm) | LSY-QB-KD005 |
Fusion time | 55-75 sec | ISO 1830-6 |
White creasing | 85 | LSY-QB-KD016 |