上海沐音新材料有限公司
LEXAN? HPB3144 resin
聚碳酸酯
产品说明:
Standard flow, transparent, high purity polycarbonate copolymer resin with reduced oxygen permeability and water vapor transmission rate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant.
| 总体 | ||||
|
材料状态
|
|
|||
|
资料1
|
||||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
特性
|
|
|||
|
用途
|
|
|||
|
机构评级
|
|
|||
|
外观
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
|||
|
--
|
1.20
|
g/cm3
|
ASTM D792 |
|
--
|
1.17
|
g/cm3
|
ISO 1183,ASTM D792 |
|
特定体积
|
0.850
|
cm3/g
|
ASTM D792 |
|
熔流率（熔体流动速率）(300°C/1.2 kg)
|
15
|
g/10 min
|
ASTM D1238 |
|
溶化体积流率（MVR）(300°C/1.2 kg)
|
13.0
|
cm3/10min
|
ISO 1133 |
|
收缩率 - 流动(3.20 mm)
|
0.50 到 0.80
|
%
|
内部方法 |
|
吸水率
|
|||
|
24 hr
|
0.080
|
%
|
ASTM D570 |
|
24 hr, 50% RH
|
0.040
|
%
|
ASTM D570 |
|
饱和, 23°C
|
0.27
|
%
|
ISO 62 |
|
平衡, 23°C
|
0.28
|
%
|
ASTM D570 |
|
平衡, 50% RH
|
0.13
|
%
|
ASTM D570 |
|
平衡, 23°C, 50% RH
|
0.13
|
%
|
ISO 62 |
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
洛氏硬度
|
ASTM D785 | ||
|
L 计秤
|
108
|
|
|
|
M 级
|
93
|
|
|
|
球压硬度(H 358/30)
|
128
|
MPa
|
ISO 2039-1 |
|
Erichson Scratch Depth - 6N
|
14.0
|
μm
|
内部方法 |
|
Pencil Hardness2
|
H
|
|
ASTM D3363 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
--3
|
2900
|
MPa
|
ASTM D638 |
|
--
|
2450
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服4
|
80.0
|
MPa
|
ASTM D638 |
|
屈服
|
80.0
|
MPa
|
ISO 527-2/50 |
|
断裂4
|
65.0
|
MPa
|
ASTM D638 |
|
断裂
|
60.0
|
MPa
|
ISO 527-2/50 |
|
伸长率
|
|||
|
屈服4
|
7.0
|
%
|
ASTM D638 |
|
屈服
|
7.0
|
%
|
ISO 527-2/50 |
|
断裂4
|
70
|
%
|
ASTM D638 |
|
断裂
|
40
|
%
|
ISO 527-2/50 |
|
弯曲模量
|
|||
|
50.0 mm 跨距5
|
2600
|
MPa
|
ASTM D790 |
|
--6
|
2450
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
--6,7
|
108
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距5
|
120
|
MPa
|
ASTM D790 |
|
泰伯耐磨性
|
|||
|
1000 Cycles, 1000 g, CS-17 转轮
|
10.0
|
mg
|
ASTM D1044 |
|
1000 Cycles, 1000 g, CS-17 转轮
|
10.0
|
mg
|
内部方法 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度8
|
ISO 179/1eA | ||
|
-30°C
|
3.0
|
kJ/m2
|
|
|
23°C
|
3.0
|
kJ/m2
|
|
|
简支梁无缺口冲击强度8
|
ISO 179/1eU | ||
|
-30°C
|
47
|
kJ/m2
|
|
|
23°C
|
无断裂
|
|
|
|
悬壁梁缺口冲击强度
|
|||
|
-30°C
|
30
|
J/m
|
ASTM D256 |
|
23°C
|
30
|
J/m
|
ASTM D256 |
|
-30°C9
|
4.0
|
kJ/m2
|
ISO 180/1A |
|
23°C9
|
5.0
|
kJ/m2
|
ISO 180/1A |
|
无缺口悬臂梁冲击
|
|||
|
23°C
|
无断裂
|
|
ASTM D4812,ISO 180/1U |
|
-30°C9
|
45
|
kJ/m2
|
ISO 180/1U |
|
装有测量仪表的落镖冲击(23°C, Total Energy)
|
30.0
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
0.45 MPa, 未退火, 3.20 mm
|
133
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 100 mm 跨距10
|
131
|
°C
|
ISO 75-2/Be |
|
1.8 MPa, 未退火, 3.20 mm
|
119
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 100 mm 跨距10
|
118
|
°C
|
ISO 75-2/Ae |
|
维卡软化温度
|
|||
|
--
|
139
|
°C
|
ASTM D152511 |
|
--
|
138
|
°C
|
ISO 306/B50 |
|
--
|
140
|
°C
|
ISO 306/B120 |
|
Ball Pressure Test
|
IEC 60695-10-2 | ||
|
125°C
|
Pass
|
|
|
|
140°C12
|
Pass
|
|
|
|
线形热膨胀系数
|
|||
|
流动 : -40 到 95°C
|
7.0E-5
|
cm/cm/°C
|
ASTM E831 |
|
流动 : 23 到 80°C
|
7.0E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
横向 : -40 到 95°C
|
7.0E-5
|
cm/cm/°C
|
ASTM E831 |
|
横向 : 23 到 80°C
|
7.0E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
比热
|
1400
|
J/kg/°C
|
ASTM C351 |
|
导热系数
|
0.20
|
W/m/K
|
ASTM C177,ISO 8302 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
体积电阻率
|
1.0E+17
|
ohm·cm
|
ASTM D257 |
|
介电常数
|
ASTM D150 | ||
|
50 Hz
|
2.90
|
|
|
|
60 Hz
|
2.90
|
|
|
|
1 MHz
|
2.80
|
|
|
|
相比耐漏电起痕指数(CTI)
|
PLC 2
|
|
UL 746 |
| 光学性能 |
额定值
|
单位制
|
测试方法
|
|
折射率
|
1.584
|
|
ASTM D542,ISO 489 |
|
透射率(2540 μm)
|
88.0
|
%
|
ASTM D1003 |
|
雾度(2540 μm)
|
0.80
|
%
|
ASTM D1003 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
120
|
°C
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
料斗温度
|
60.0 到 80.0
|
°C
|
|
|
料筒后部温度
|
260 到 280
|
°C
|
|
|
料筒中部温度
|
280 到 305
|
°C
|
|
|
料筒前部温度
|
295 到 315
|
°C
|
|
|
射嘴温度
|
290 到 310
|
°C
|
|
|
加工（熔体）温度
|
295 到 315
|
°C
|
|
|
模具温度
|
70.0 到 95.0
|
°C
|
| 备注 |
 |