LEXAN? HP2 resin
聚碳酸酯
产品说明:
Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains mold release.
| 总体 | ||||
|
材料状态
|
|
|||
|
资料1
|
||||
|
UL 黄卡2
|
||||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
添加剂
|
|
|||
|
特性
|
|
|||
|
用途
|
|
|||
|
机构评级
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
ASTM D792 | ||
|
--
|
1.20
|
g/cm3
|
|
|
--
|
1.19
|
g/cm3
|
|
|
特定体积
|
0.830
|
cm3/g
|
ASTM D792 |
|
熔流率（熔体流动速率）(300°C/1.2 kg)
|
18
|
g/10 min
|
ASTM D1238 |
|
溶化体积流率（MVR）(300°C/1.2 kg)
|
16.0
|
cm3/10min
|
ISO 1133 |
|
收缩率 - 流动(3.20 mm)
|
0.50 到 0.70
|
%
|
内部方法 |
|
吸水率
|
ASTM D570 | ||
|
24 hr
|
0.15
|
%
|
|
|
平衡, 23°C
|
0.35
|
%
|
|
|
平衡, 100°C
|
0.58
|
%
|
|
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
洛氏硬度
|
ASTM D785 | ||
|
M 级
|
70
|
|
|
|
R 级
|
118
|
|
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
--3
|
2370
|
MPa
|
ASTM D638 |
|
--
|
2350
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服4
|
62.0
|
MPa
|
ASTM D638 |
|
屈服
|
63.0
|
MPa
|
ISO 527-2/50 |
|
断裂4
|
68.0
|
MPa
|
ASTM D638 |
|
断裂
|
65.0
|
MPa
|
ISO 527-2/50 |
|
伸长率
|
|||
|
屈服4
|
7.0
|
%
|
ASTM D638 |
|
屈服
|
6.0
|
%
|
ISO 527-2/50 |
|
断裂4
|
130
|
%
|
ASTM D638 |
|
断裂
|
100
|
%
|
ISO 527-2/50 |
|
弯曲模量
|
|||
|
50.0 mm 跨距5
|
2340
|
MPa
|
ASTM D790 |
|
--6
|
2300
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
--6,7
|
90.0
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距5
|
96.0
|
MPa
|
ASTM D790 |
|
泰伯耐磨性(1000 Cycles, 1000 g, CS-17 转轮)
|
10.0
|
mg
|
ASTM D1044 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度(23°C)
|
35
|
kJ/m2
|
ISO 179/2C |
|
悬壁梁缺口冲击强度
|
|||
|
23°C
|
690
|
J/m
|
ASTM D256 |
|
-30°C8
|
10
|
kJ/m2
|
ISO 180/1A |
|
23°C8
|
12
|
kJ/m2
|
ISO 180/1A |
|
无缺口悬臂梁冲击(23°C)
|
3200
|
J/m
|
ASTM D4812 |
|
装有测量仪表的落镖冲击(23°C, Energy at Peak Load)
|
62.0
|
J
|
ASTM D3763 |
|
落锤冲击(23°C)
|
169
|
J
|
ASTM D3029 |
|
拉伸冲击强度9
|
546
|
kJ/m2
|
ASTM D1822 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
0.45 MPa, 未退火, 6.40 mm
|
137
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 100 mm 跨距10
|
133
|
°C
|
ISO 75-2/Be |
|
1.8 MPa, 未退火, 6.40 mm
|
129
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 100 mm 跨距10
|
122
|
°C
|
ISO 75-2/Ae |
|
维卡软化温度
|
|||
|
--
|
154
|
°C
|
ASTM D152511 |
|
--
|
140
|
°C
|
ISO 306/B50 |
|
--
|
141
|
°C
|
ISO 306/B120 |
|
Ball Pressure Test(125°C)
|
Pass
|
|
IEC 60695-10-2 |
|
线形热膨胀系数 - 流动
|
|||
|
-40 到 95°C
|
6.8E-5
|
cm/cm/°C
|
ASTM E831 |
|
23 到 80°C
|
7.0E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
比热
|
1250
|
J/kg/°C
|
ASTM C351 |
|
导热系数
|
|||
|
--
|
0.19
|
W/m/K
|
ASTM C177 |
|
--
|
0.20
|
W/m/K
|
ISO 8302 |
|
RTI Elec
|
130
|
°C
|
UL 746 |
|
RTI Imp
|
130
|
°C
|
UL 746 |
|
RTI
|
130
|
°C
|
UL 746 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
1.0E+15
|
ohm
|
IEC 60093 |
|
体积电阻率
|
|||
|
--
|
1.0E+17
|
ohm·cm
|
ASTM D257 |
|
--
|
1.0E+15
|
ohm·cm
|
IEC 60093 |
|
介电强度
|
|||
|
3.20 mm, in Air
|
15
|
kV/mm
|
ASTM D149 |
|
3.20 mm, 在油中
|
17
|
kV/mm
|
IEC 60243-1 |
|
介电常数
|
|||
|
50 Hz
|
3.17
|
|
ASTM D150 |
|
60 Hz
|
3.17
|
|
ASTM D150 |
|
1 MHz
|
2.96
|
|
ASTM D150 |
|
50 Hz
|
2.70
|
|
IEC 60250 |
|
60 Hz
|
2.70
|
|
IEC 60250 |
|
1 MHz
|
2.70
|
|
IEC 60250 |
|
耗散因数
|
|||
|
50 Hz
|
9.0E-4
|
|
ASTM D150 |
|
60 Hz
|
9.0E-4
|
|
ASTM D150 |
|
1 MHz
|
0.010
|
|
ASTM D150,IEC 60250 |
|
50 Hz
|
1.0E-3
|
|
IEC 60250 |
|
60 Hz
|
1.0E-3
|
|
IEC 60250 |
|
相比耐漏电起痕指数(CTI)
|
PLC 2
|
|
UL 746 |
|
高电弧燃烧指数(HAI)
|
PLC 1
|
|
UL 746 |
|
高电压电弧起痕速率 (HVTR)
|
PLC 2
|
|
UL 746 |
|
热丝引燃 (HWI)
|
PLC 2
|
|
UL 746 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级(1.47 mm)
|
HB
|
|
UL 94 |
|
极限氧指数
|
25
|
%
|
ISO 4589-2 |
| 光学性能 |
额定值
|
单位制
|
测试方法
|
|
折射率
|
1.586
|
|
ASTM D542 |
|
透射率(2540 μm)
|
88.0
|
%
|
ASTM D1003 |
|
雾度(2540 μm)
|
1.0
|
%
|
ASTM D1003 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
121
|
°C
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
干燥时间，最大
|
48
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 60
|
%
|
|
|
料筒后部温度
|
260 到 282
|
°C
|
|
|
料筒中部温度
|
271 到 293
|
°C
|
|
|
料筒前部温度
|
282 到 304
|
°C
|
|
|
射嘴温度
|
277 到 299
|
°C
|
|
|
加工（熔体）温度
|
282 到 304
|
°C
|
|
|
模具温度
|
71.1 到 93.3
|
°C
|
|
|
背压
|
0.345 到 0.689
|
MPa
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
0.025 到 0.076
|
mm
|
| 备注 |
 |