上海沐音新材料有限公司
SABIC? PC FL405 resin
聚碳酸酯
产品说明:
Various weight reductions at 0.250" (6.38 mm) wall. Impact resistant, superior processing, excellent surface. UL94 V-0 at 0.120
| 总体 | ||||
|
材料状态
|
|
|||
|
资料 1
|
||||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
特性
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
ASTM D792 | ||
|
-- 2
|
1.08
|
g/cm3
|
|
|
--
|
1.20
|
g/cm3
|
|
|
收缩率 - 流动 (6.40 mm)
|
0.60 到 0.80
|
%
|
内部方法 |
|
吸水率
|
ASTM D570 | ||
|
24 hr
|
0.14
|
%
|
|
|
平衡, 23°C
|
0.31
|
%
|
|
|
Foam - Physical 3
|
10
|
%
|
内部方法 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量 (6.40 mm)
|
2100
|
MPa
|
ASTM D638 |
|
抗张强度 (屈服, 6.35 mm)
|
54.5
|
MPa
|
ASTM D638 |
|
伸长率 (断裂, 6.35 mm)
|
7.2
|
%
|
ASTM D638 |
|
弯曲模量 (6.40 mm)
|
2480
|
MPa
|
ASTM D790 |
|
弯曲强度 (屈服, 6.40 mm)
|
86.2
|
MPa
|
ASTM D790 |
|
Foam - Mechanical 3
|
10
|
%
|
内部方法 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
无缺口悬臂梁冲击 (23°C)
|
2700
|
J/m
|
ASTM D4812 |
|
落锤冲击 (23°C)
|
61.0
|
J
|
内部方法 |
|
Foam - Impact 3
|
10
|
%
|
内部方法 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
ASTM D648 | ||
|
0.45 MPa, 未退火, 6.40 mm
|
138
|
°C
|
|
|
1.8 MPa, 未退火, 6.40 mm
|
127
|
°C
|
|
|
线形热膨胀系数 - 流动 (-40 到 95°C)
|
6.7E-5
|
cm/cm/°C
|
ASTM E831 |
|
比热
|
1340
|
J/kg/°C
|
ASTM C351 |
|
RTI Elec
|
80.0
|
°C
|
UL 746 |
|
RTI Imp
|
80.0
|
°C
|
UL 746 |
|
RTI
|
80.0
|
°C
|
UL 746 |
|
Foam - Thermal 3
|
10
|
%
|
内部方法 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
> 1.1E+17
|
ohm
|
ASTM D257 |
|
体积电阻率
|
3.5E+17
|
ohm·cm
|
ASTM D257 |
|
介电常数
|
ASTM D150 | ||
|
100 Hz
|
2.42
|
|
|
|
1 MHz
|
2.43
|
|
|
|
耗散因数
|
ASTM D150 | ||
|
100 Hz
|
1.1E-3
|
|
|
|
1 MHz
|
4.4E-3
|
|
|
|
Foam - Electrical 3
|
20
|
%
|
内部方法 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级
|
UL 94 | ||
|
3.05 mm
|
V-0
|
|
|
|
6.10 mm
|
5VA
|
|
|
|
极限氧指数
|
39
|
%
|
ASTM D2863 |
|
Foam - Flame Class Minimum Density
|
1.060
|
g/cm3
|
内部方法 |
|
Radiant Panel Listing (UL)
|
YES
|
|
| 补充信息 | |||
|
Structural Foam Molding - Blowing Agent, Chemical System: FLC298 Structural Foam Molding - Blowing Agent, Physical System: Nitrogen Gas Structural Foam Molding - Concentration Range (Blowing Agent): 3 - 5 % Structural Foam Molding - Drying Temperature (Blowing Agent): 104 °C Structural Foam Molding - Drying Temperature (Resin): 121 °C Structural Foam Molding - Drying Time (Blowing Agent): 4 hrs Structural Foam Molding - Drying Time (Resin): 3 - 4 hrs Structural Foam Molding - Drying Time (Resin, Cumulative): 48 hrs Structural Foam Molding - Front Temperature: 277 - 299°C Structural Foam Molding - Melt Temperature: 274 - 299 °C Structural Foam Molding - Middle Temperature: 277 - 299 °C Structural Foam Molding - Mold Temperature: 71 - 93 °C Structural Foam Molding - Nozzle Temperature: 265 - 288 °C Structural Foam Molding - Rear Temperature: 271 - 293 °C Structural Foam Molding - Recommended Concentration (Blowing Agent): 1.5 % |
| 备注 |
 |