上海沐音新材料有限公司
LEXAN? EXL9134 resin
聚碳酸酯
产品说明:
LEXAN EXL9134 polycarbonate (PC) siloxane copolymer resin is a UV stabilized high flow opaque injection molding (IM) grade. This resin offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, non-chlorine FR systems, extreme low temperature ductility (-40 deg C) characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL9134 resin is a product available in a wide range of opaque colors and may be an excellent candidate for a wide range of applications.
| 总体 | ||||
|
材料状态
|
|
|||
|
资料 1
|
||||
|
UL 黄卡 2
|
||||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
添加剂
|
|
|||
|
特性
|
|
|||
|
外观
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.19
|
g/cm3
|
ASTM D792, ISO 1183 |
|
熔流率（熔体流动速率） (300°C/1.2 kg)
|
16
|
g/10 min
|
ASTM D1238 |
|
溶化体积流率（MVR） (300°C/1.2 kg)
|
15.1
|
cm3/10min
|
ISO 1133 |
|
收缩率 - 流动 (3.20 mm)
|
0.40 到 0.80
|
%
|
内部方法 |
|
吸水率
|
ISO 62 | ||
|
饱和, 23°C
|
0.40
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.15
|
%
|
|
|
室外适用性
|
f1
|
|
UL 746C |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
-- 3
|
2100
|
MPa
|
ASTM D638 |
|
--
|
2000
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服 4
|
58.0
|
MPa
|
ASTM D638 |
|
屈服
|
56.0
|
MPa
|
ISO 527-2/50 |
|
断裂 4
|
59.0
|
MPa
|
ASTM D638 |
|
断裂
|
57.0
|
MPa
|
ISO 527-2/50 |
|
伸长率
|
|||
|
屈服 4
|
6.0
|
%
|
ASTM D638 |
|
屈服
|
6.0
|
%
|
ISO 527-2/50 |
|
断裂 4
|
120
|
%
|
ASTM D638 |
|
断裂
|
110
|
%
|
ISO 527-2/50 |
|
弯曲模量
|
|||
|
50.0 mm 跨距 5
|
2400
|
MPa
|
ASTM D790 |
|
-- 6
|
2100
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
-- 6, 7
|
87.0
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距 5
|
92.0
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度 8
|
ISO 179/1eA | ||
|
-30°C
|
35
|
kJ/m2
|
|
|
23°C
|
70
|
kJ/m2
|
|
|
简支梁无缺口冲击强度 8
|
ISO 179/1eU | ||
|
-30°C
|
无断裂
|
|
|
|
23°C
|
无断裂
|
|
|
|
悬壁梁缺口冲击强度
|
|||
|
-30°C
|
660
|
J/m
|
ASTM D256 |
|
23°C
|
790
|
J/m
|
ASTM D256 |
|
-30°C 9
|
30
|
kJ/m2
|
ISO 180/1A |
|
23°C 9
|
65
|
kJ/m2
|
ISO 180/1A |
|
无缺口伊佐德冲击强度 9
|
ISO 180/1U | ||
|
-30°C
|
无断裂
|
|
|
|
23°C
|
无断裂
|
|
|
|
装有测量仪表的落镖冲击 (23°C, Total Energy)
|
67.0
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
1.8 MPa, 未退火, 3.20 mm
|
123
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 64.0 mm 跨距 10
|
118
|
°C
|
ISO 75-2/Af |
|
维卡软化温度
|
|||
|
--
|
140
|
°C
|
ASTM D1525 11 |
|
--
|
139
|
°C
|
ISO 306/B50 |
|
--
|
141
|
°C
|
ISO 306/B120 |
|
线形热膨胀系数
|
ASTM E831, ISO 11359-2 | ||
|
流动 : -40 到 40°C
|
6.1E-5
|
cm/cm/°C
|
|
|
横向 : -40 到 40°C
|
6.2E-5
|
cm/cm/°C
|
|
|
RTI Elec
|
125
|
°C
|
UL 746 |
|
RTI Imp
|
115
|
°C
|
UL 746 |
|
RTI
|
120
|
°C
|
UL 746 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级
|
UL 94 | ||
|
1.50 mm
|
V-0
|
|
|
|
3.00 mm
|
5VA
|
|
|
|
灼热丝易燃指数 (1.50 mm)
|
960
|
°C
|
IEC 60695-2-12 |
|
热灯丝点火温度
|
IEC 60695-2-13 | ||
|
1.50 mm
|
825
|
°C
|
|
|
3.00 mm
|
825
|
°C
|
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
120
|
°C
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
干燥时间，最大
|
48
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 60
|
%
|
|
|
料筒后部温度
|
270 到 295
|
°C
|
|
|
料筒中部温度
|
280 到 305
|
°C
|
|
|
料筒前部温度
|
295 到 315
|
°C
|
|
|
射嘴温度
|
290 到 310
|
°C
|
|
|
加工（熔体）温度
|
295 到 315
|
°C
|
|
|
模具温度
|
70.0 到 95.0
|
°C
|
|
|
背压
|
0.300 到 0.700
|
MPa
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
0.025 到 0.076
|
mm
|
| 备注 |
 |