LEXAN? EXL4019 resin
聚碳酸酯
9.0% 玻璃纤维增强材料
产品说明:
LEXAN EXL4019 is an opaque 9% Glass Fiber (GF) reinforced polycarbonate (PC) siloxane copolymer resin for injection molding (IM) applications requiring improved stiffness. This resin also offers improved ductility over conventional GF reinforced PC resins in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times when compared to standard PC. LEXAN EXL4019 resin is a product that may be an excellent candidate for a wide variety of applications. Available in limited colors only.
| 总体 | ||||
|
材料状态
|
|
|||
|
资料 1
|
||||
|
UL 黄卡 2
|
||||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
填料/增强材料
|
|
|||
|
特性
|
|
|||
|
外观
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.25
|
g/cm3
|
ASTM D792, ISO 1183 |
|
熔流率（熔体流动速率） (300°C/1.2 kg)
|
7.5
|
g/10 min
|
ASTM D1238 |
|
溶化体积流率（MVR） (300°C/1.2 kg)
|
6.50
|
cm3/10min
|
ISO 1133 |
|
收缩率
|
内部方法 | ||
|
流动 : 3.20 mm
|
0.20 到 0.60
|
%
|
|
|
横向流动 : 3.20 mm
|
0.20 到 0.60
|
%
|
|
|
吸水率
|
ISO 62 | ||
|
饱和, 23°C
|
0.15
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.40
|
%
|
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
-- 3
|
3950
|
MPa
|
ASTM D638 |
|
--
|
3900
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服 4
|
55.0
|
MPa
|
ASTM D638 |
|
屈服
|
54.0
|
MPa
|
ISO 527-2/5 |
|
断裂 4
|
45.0
|
MPa
|
ASTM D638 |
|
断裂
|
48.0
|
MPa
|
ISO 527-2/5 |
|
伸长率
|
|||
|
屈服 4
|
4.3
|
%
|
ASTM D638 |
|
屈服
|
4.3
|
%
|
ISO 527-2/5 |
|
断裂 4
|
14
|
%
|
ASTM D638 |
|
断裂
|
8.7
|
%
|
ISO 527-2/5 |
|
弯曲模量
|
|||
|
50.0 mm 跨距 5
|
3500
|
MPa
|
ASTM D790 |
|
-- 6
|
3450
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
-- 6, 7
|
98.0
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距 5
|
103
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度 8
|
ISO 179/1eA | ||
|
-30°C
|
15
|
kJ/m2
|
|
|
23°C
|
25
|
kJ/m2
|
|
|
简支梁无缺口冲击强度 8
|
ISO 179/1eU | ||
|
-30°C
|
无断裂
|
|
|
|
23°C
|
无断裂
|
|
|
|
悬壁梁缺口冲击强度
|
|||
|
-30°C
|
150
|
J/m
|
ASTM D256 |
|
23°C
|
350
|
J/m
|
ASTM D256 |
|
-30°C 9
|
10
|
kJ/m2
|
ISO 180/1A |
|
23°C 9
|
25
|
kJ/m2
|
ISO 180/1A |
|
无缺口伊佐德冲击强度 9
|
ISO 180/1U | ||
|
-30°C
|
无断裂
|
|
|
|
23°C
|
无断裂
|
|
|
|
装有测量仪表的落镖冲击 (23°C, Total Energy)
|
40.0
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
1.8 MPa, 未退火, 3.20 mm
|
137
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 100 mm 跨距 10
|
135
|
°C
|
ISO 75-2/Ae |
|
维卡软化温度
|
146
|
°C
|
ASTM D1525 11, ISO 306/B50, ISO 306/B120 |
|
Ball Pressure Test (75°C)
|
Pass
|
|
IEC 60695-10-2 |
|
线形热膨胀系数
|
ASTM E831, ISO 11359-2 | ||
|
流动 : -40 到 40°C
|
4.7E-5
|
cm/cm/°C
|
|
|
横向 : -40 到 40°C
|
7.0E-5
|
cm/cm/°C
|
| 可燃性 |
额定值
|
|
测试方法
|
|
UL 阻燃等级 (0.750 mm)
|
HB
|
|
UL 94 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
121
|
°C
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
干燥时间，最大
|
48
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 60
|
%
|
|
|
料筒后部温度
|
288 到 310
|
°C
|
|
|
料筒中部温度
|
299 到 321
|
°C
|
|
|
料筒前部温度
|
310 到 332
|
°C
|
|
|
射嘴温度
|
304 到 327
|
°C
|
|
|
加工（熔体）温度
|
310 到 332
|
°C
|
|
|
模具温度
|
82.0 到 116
|
°C
|
|
|
背压
|
0.345 到 0.689
|
MPa
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
0.025 到 0.076
|
mm
|
| 备注 |
 |