LEXAN? EXL1443T resin
聚碳酸酯
产品说明:
LEXAN EXL1443T polycarbonate (PC) siloxane copolymer resin is an injection molding grade with FDA and EU food contact compliance. This resin offers excellent low temperature (-30 C) ductility in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1443T resin is available in transparent and opaque colors and is an excellent candidate for a broad range of food contact applications.
总体 | ||||
材料状态
|
|
|||
资料 1
|
||||
UL 黄卡 2
|
||||
搜索 UL 黄卡
|
|
|||
供货地区
|
|
|||
特性
|
|
|||
用途
|
|
|||
机构评级
|
|
|||
外观
|
|
|||
加工方法
|
|
物理性能 |
额定值
|
单位制
|
测试方法
|
比重
|
1.19
|
g/cm3
|
ASTM D792, ISO 1183 |
熔流率(熔体流动速率) (300°C/1.2 kg)
|
10
|
g/10 min
|
ASTM D1238 |
溶化体积流率(MVR) (300°C/1.2 kg)
|
9.50
|
cm3/10min
|
ISO 1133 |
收缩率
|
内部方法 | ||
流动 : 3.20 mm
|
0.40 到 0.80
|
%
|
|
横向流动 : 3.20 mm
|
0.40 到 0.80
|
%
|
|
吸水率
|
ISO 62 | ||
饱和, 23°C
|
0.12
|
%
|
|
平衡, 23°C, 50% RH
|
0.093
|
%
|
|
硬度 |
额定值
|
单位制
|
测试方法
|
洛氏硬度 (L 计秤)
|
90
|
|
ASTM D785 |
机械性能 |
额定值
|
单位制
|
测试方法
|
拉伸模量
|
|||
-- 3
|
2220
|
MPa
|
ASTM D638 |
--
|
2350
|
MPa
|
ISO 527-2/1 |
抗张强度
|
|||
屈服 4
|
58.0
|
MPa
|
ASTM D638 |
屈服
|
57.9
|
MPa
|
ISO 527-2/50 |
断裂 4
|
64.1
|
MPa
|
ASTM D638 |
断裂
|
61.5
|
MPa
|
ISO 527-2/50 |
伸长率
|
|||
屈服 4
|
5.8
|
%
|
ASTM D638 |
屈服
|
5.5
|
%
|
ISO 527-2/50 |
断裂 4
|
130
|
%
|
ASTM D638 |
断裂
|
120
|
%
|
ISO 527-2/50 |
弯曲模量
|
|||
50.0 mm 跨距 5
|
2220
|
MPa
|
ASTM D790 |
-- 6
|
2150
|
MPa
|
ISO 178 |
弯曲应力
|
|||
-- 6, 7
|
90.2
|
MPa
|
ISO 178 |
屈服, 50.0 mm 跨距 5
|
94.3
|
MPa
|
ASTM D790 |
冲击性能 |
额定值
|
单位制
|
测试方法
|
简支梁缺口冲击强度 8
|
ISO 179/1eA | ||
-30°C
|
50
|
kJ/m2
|
|
23°C
|
70
|
kJ/m2
|
|
简支梁无缺口冲击强度 8
|
ISO 179/1eU | ||
-30°C
|
无断裂
|
|
|
23°C
|
无断裂
|
|
|
悬壁梁缺口冲击强度
|
|||
-30°C
|
800
|
J/m
|
ASTM D256 |
23°C
|
890
|
J/m
|
ASTM D256 |
-30°C 9
|
45
|
kJ/m2
|
ISO 180/1A |
23°C 9
|
65
|
kJ/m2
|
ISO 180/1A |
无缺口伊佐德冲击强度 9
|
ISO 180/1U | ||
-30°C
|
无断裂
|
|
|
23°C
|
无断裂
|
|
|
装有测量仪表的落镖冲击
|
ASTM D3763 | ||
-30°C, Total Energy
|
85.0
|
J
|
|
23°C, Total Energy
|
82.4
|
J
|
热性能 |
额定值
|
单位制
|
测试方法
|
载荷下热变形温度
|
|||
1.8 MPa, 未退火, 3.20 mm
|
124
|
°C
|
ASTM D648 |
1.8 MPa, 未退火, 64.0 mm 跨距 10
|
119
|
°C
|
ISO 75-2/Af |
维卡软化温度
|
|||
--
|
141
|
°C
|
ASTM D1525 11, ISO 306/B50 11 |
--
|
142
|
°C
|
ISO 306/B120 |
Ball Pressure Test (125°C)
|
Pass
|
|
IEC 60695-10-2 |
线形热膨胀系数
|
|||
流动 : -40 到 95°C
|
7.2E-5
|
cm/cm/°C
|
ASTM E831 |
流动 : 23 到 80°C
|
7.2E-5
|
cm/cm/°C
|
ISO 11359-2 |
横向 : -40 到 95°C
|
7.9E-5
|
cm/cm/°C
|
ASTM E831 |
横向 : 23 到 80°C
|
7.9E-5
|
cm/cm/°C
|
ISO 11359-2 |
RTI Elec
|
130
|
°C
|
UL 746 |
RTI
|
130
|
°C
|
UL 746 |
电气性能 |
额定值
|
单位制
|
测试方法
|
表面电阻率
|
> 1.0E+15
|
ohm
|
ASTM D257 |
体积电阻率
|
> 1.0E+15
|
ohm·cm
|
ASTM D257 |
可燃性 |
额定值
|
单位制
|
测试方法
|
UL 阻燃等级
|
UL 94 | ||
2.50 mm
|
V-2
|
|
|
3.00 mm, Testing by SABIC
|
V-2
|
|
|
灼热丝易燃指数 (3.00 mm)
|
960
|
°C
|
IEC 60695-2-12 |
热灯丝点火温度
|
IEC 60695-2-13 | ||
0.800 mm
|
825
|
°C
|
|
3.00 mm
|
825
|
°C
|
光学性能 |
额定值
|
单位制
|
测试方法
|
透射率 (2540 μm)
|
82.0
|
%
|
ASTM D1003 |
雾度 (2540 μm)
|
3.0
|
%
|
ASTM D1003 |
注射 |
额定值
|
单位制
|
|
干燥温度
|
121
|
°C
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
干燥时间,最大
|
48
|
hr
|
|
建议的最大水分含量
|
0.020
|
%
|
|
建议注射量
|
40 到 60
|
%
|
|
料筒后部温度
|
217 到 293
|
°C
|
|
料筒中部温度
|
282 到 304
|
°C
|
|
料筒前部温度
|
293 到 316
|
°C
|
|
射嘴温度
|
288 到 310
|
°C
|
|
加工(熔体)温度
|
293 到 316
|
°C
|
|
模具温度
|
71.0 到 93.0
|
°C
|
|
背压
|
0.345 到 0.689
|
MPa
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
排气孔深度
|
0.025 到 0.076
|
mm
|
备注 |