LEXAN? EXL1330 resin
聚碳酸酯
产品说明:
LEXAN EXL1330 polycarbonate (PC) siloxane copolymer resin is a UV stabilized opaque injection molding (IM) and sheet extrusion grade. This resin offers extreme low temperature (-60 C) ductility in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1330 resin is a general purpose product available in a wide range of opaque colors and is an excellent candidate for a broad range of applications.
| 总体 | ||||
|
材料状态
|
|
|||
|
资料 1
|
||||
|
UL 黄卡 2
|
||||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
添加剂
|
|
|||
|
特性
|
|
|||
|
用途
|
|
|||
|
外观
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.18
|
g/cm3
|
ASTM D792, ISO 1183 |
|
熔流率（熔体流动速率） (300°C/1.2 kg)
|
10
|
g/10 min
|
ASTM D1238 |
|
溶化体积流率（MVR） (300°C/1.2 kg)
|
9.00
|
cm3/10min
|
ISO 1133 |
|
收缩率
|
内部方法 | ||
|
流动 : 3.20 mm
|
0.40 到 0.80
|
%
|
|
|
横向流动 : 3.20 mm
|
0.40 到 0.80
|
%
|
|
|
吸水率
|
ISO 62 | ||
|
饱和, 23°C
|
0.35
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.15
|
%
|
|
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
球压硬度 (H 358/30)
|
90.0
|
MPa
|
ISO 2039-1 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
-- 3
|
2100
|
MPa
|
ASTM D638 |
|
--
|
2100
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服 4
|
58.6
|
MPa
|
ASTM D638 |
|
屈服
|
55.0
|
MPa
|
ISO 527-2/50 |
|
断裂 4
|
61.4
|
MPa
|
ASTM D638 |
|
断裂
|
56.0
|
MPa
|
ISO 527-2/50 |
|
伸长率
|
|||
|
屈服 4
|
6.0
|
%
|
ASTM D638 |
|
屈服
|
5.0
|
%
|
ISO 527-2/50 |
|
断裂 4
|
130
|
%
|
ASTM D638 |
|
断裂
|
> 100
|
%
|
ISO 527-2/50 |
|
弯曲模量
|
|||
|
50.0 mm 跨距 5
|
2070
|
MPa
|
ASTM D790 |
|
-- 6
|
2100
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
-- 6, 7
|
85.0
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距 5
|
88.9
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度 8
|
ISO 179/1eA | ||
|
-30°C
|
60
|
kJ/m2
|
|
|
23°C
|
75
|
kJ/m2
|
|
|
简支梁无缺口冲击强度 8
|
ISO 179/1eU | ||
|
-30°C
|
无断裂
|
|
|
|
23°C
|
无断裂
|
|
|
|
悬壁梁缺口冲击强度
|
|||
|
-50°C
|
590
|
J/m
|
ASTM D256 |
|
-30°C
|
680
|
J/m
|
ASTM D256 |
|
23°C
|
800
|
J/m
|
ASTM D256 |
|
23°C, 6.40 mm
|
640
|
J/m
|
ASTM D256 |
|
-30°C 9
|
55
|
kJ/m2
|
ISO 180/1A |
|
23°C 9
|
70
|
kJ/m2
|
ISO 180/1A |
|
无缺口悬臂梁冲击
|
|||
|
23°C 10
|
1100
|
J/m
|
内部方法 |
|
-30°C 9
|
无断裂
|
|
ISO 180/1U |
|
23°C 9
|
无断裂
|
|
ISO 180/1U |
|
装有测量仪表的落镖冲击 (23°C, Total Energy)
|
52.9
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
0.45 MPa, 未退火, 3.20 mm
|
134
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 100 mm 跨距 11
|
136
|
°C
|
ISO 75-2/Be |
|
1.8 MPa, 未退火, 3.20 mm
|
121
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 6.40 mm
|
124
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 100 mm 跨距 11
|
125
|
°C
|
ISO 75-2/Ae |
|
维卡软化温度
|
|||
|
--
|
143
|
°C
|
ASTM D1525 12, ISO 306/B50 12 |
|
--
|
145
|
°C
|
ISO 306/B120 |
|
Ball Pressure Test (125°C)
|
Pass
|
|
IEC 60695-10-2 |
|
线形热膨胀系数
|
|||
|
流动 : -40 到 40°C
|
6.7E-5
|
cm/cm/°C
|
ASTM E831 |
|
流动 : 23 到 80°C
|
7.2E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
横向 : -40 到 40°C
|
6.7E-5
|
cm/cm/°C
|
ASTM E831 |
|
横向 : 23 到 80°C
|
7.2E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
RTI Elec
|
125
|
°C
|
UL 746 |
|
RTI Imp
|
115
|
°C
|
UL 746 |
|
RTI
|
120
|
°C
|
UL 746 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级 (0.800 mm)
|
HB
|
|
UL 94 |
|
灼热丝易燃指数
|
IEC 60695-2-12 | ||
|
0.800 mm
|
850
|
°C
|
|
|
1.00 mm
|
960
|
°C
|
|
|
热灯丝点火温度
|
IEC 60695-2-13 | ||
|
1.00 mm
|
875
|
°C
|
|
|
3.00 mm
|
875
|
°C
|
|
|
极限氧指数
|
35
|
%
|
ISO 4589-2 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
121
|
°C
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
干燥时间，最大
|
48
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 60
|
%
|
|
|
料筒后部温度
|
217 到 293
|
°C
|
|
|
料筒中部温度
|
282 到 304
|
°C
|
|
|
料筒前部温度
|
293 到 316
|
°C
|
|
|
射嘴温度
|
288 到 310
|
°C
|
|
|
加工（熔体）温度
|
293 到 316
|
°C
|
|
|
模具温度
|
71.0 到 93.0
|
°C
|
|
|
背压
|
0.345 到 0.689
|
MPa
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
0.025 到 0.076
|
mm
|
|
| 挤出 |
额定值
|
单位制
|
|
|
干燥温度
|
110 到 121
|
°C
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
料筒1区温度
|
249 到 288
|
°C
|
|
|
料筒2区温度
|
243 到 271
|
°C
|
|
|
料筒3区温度
|
227 到 254
|
°C
|
|
|
接头温度
|
227 到 254
|
°C
|
|
|
熔体温度
|
243 到 260
|
°C
|
|
|
口模温度
|
238 到 260
|
°C
|
|
| 挤压说明 | |||
|
Drying Time (Cumulative): 48 hrs Roll Stack Temp - Bottom: 121 - 143 °C Roll Stack Temp - Middle: 82 - 127 °C Roll Stack Temp - Top: 77 - 116 °C |
|||