Surlyn? 8940
乙烯甲基丙烯酸
产品说明：
Surlyn? 8940 is a sodium ionomer thermoplastic resin. It is available for use in conventional extrusion and injection equipment, to create various sheets or shapes.
Surlyn? 8940 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions.
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
0.950 |
g/cm3 |
ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) |
2.8 |
g/10 min |
ASTM D1238, ISO 1133 |
| 离子类型 |
Sodium |
|
|
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 抗磨损性 - NBS Index |
370 |
|
ASTM D1630 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| Freezing Point |
|
|
|
| -- |
59 |
°C |
ISO 3146 |
| -- |
59 |
°C |
ASTM D3418 |
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 肖氏硬度 (邵氏 D) |
65 |
|
ASTM D2240, ISO 868 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 抗张强度 (断裂, 23°C) |
33.0 |
MPa |
ASTM D638, ISO 527-2 |
| 伸长率 (断裂, 23°C) |
470 |
% |
ASTM D638, ISO 527-2 |
| 弯曲模量 |
|
|
ASTM D790 |
| -20°C |
717 |
MPa |
ASTM D790 |
| 23°C |
350 |
MPa |
ASTM D790 |
| 弯曲强度 (屈服) |
15.0 |
MPa |
ASTM D790 |
| 弹性体 |
额定值 |
单位制 |
测试方法 |
| 撕裂强度 (23°C) |
1.48 |
kN/m |
ASTM D624 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 悬壁梁缺口冲击强度 (23°C) |
1000 |
J/m |
ASTM D256 |
| 拉伸冲击强度 |
|
|
ASTM D1822 |
| -40°C |
757 |
kJ/m2 |
ASTM D1822 |
| 23°C |
1020 |
kJ/m2 |
ASTM D1822 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 脆化温度 |
-106 |
°C |
ASTM D746 |
| 维卡软化温度 |
63.0 |
°C |
ASTM D1525, ISO 306 |
| 熔融峰值温度 |
94.0 |
°C |
ASTM D3418, ISO 3146 |
| 光学性能 |
额定值 |
单位制 |
测试方法 |
| 雾度 (6350 μm) |
5.0 |
% |
ASTM D1003 |
| 注射 |
额定值 |
单位制 |
|
| 加工（熔体）温度 |
185 到 285 |
°C |
|