Surlyn? 8920
乙烯甲基丙烯酸
DuPont Packaging & Industrial Polymers
产品说明：
Surlyn? 8920 is a sodium ionomer thermoplastic resin. It is available for use in conventional extrusion and injection equipment, to create various sheets or shapes.
Surlyn? 8920 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions.
Surlyn? 8920 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions.
| 基本信息 | |
|---|---|
| 特性 |
|
| 机构评级 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.950 | g/cm3 | ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 0.90 | g/10 min | ASTM D1238, ISO 1133 |
| 离子类型 | Sodium |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗磨损性 - NBS Index | 640 | ASTM D1630 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| Freezing Point | |||
| -- | 48 | °C | ISO 3146 |
| -- | 48 | °C | ASTM D3418 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 66 | ASTM D2240, ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 | |||
| 屈服, 23°C, 模压成型 1 | 15.2 | MPa | ASTM D638 |
| 断裂, 23°C | 37.2 | MPa | ASTM D638, ISO 527-2 |
| 伸长率 (断裂, 23°C) | 350 | % | ASTM D638, ISO 527-2 |
| 弯曲模量 | ASTM D790 | ||
| -20°C | 670 | MPa | ASTM D790 |
| 23°C | 380 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 (23°C) | 12 | J/m | ASTM D256 |
| 拉伸冲击强度 | ASTM D1822 | ||
| -40°C | 345 | kJ/m2 | ASTM D1822 |
| 23°C | 410 | kJ/m2 | ASTM D1822 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 维卡软化温度 | 58.0 | °C | ASTM D1525, ISO 306 |
| 熔融峰值温度 | 88.0 | °C | ASTM D3418, ISO 3146 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 雾度 (6350 μm) | 4.0 | % | ASTM D1003 |
| 备注 | |
|---|---|
| 1 . | 类型 4, 50 mm/min |