上海沐音新材料有限公司
LEXAN? EXL1112T resin
聚碳酸酯
产品说明:
LEXAN* EXL1112T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding (IM) grade. This resin offers good low temperature (-20 C) ductility in combination with high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC resins. LEXAN EXL1112T resin is a genral purpose product available in transparent and opaque colors.
| 总体 | ||||
|
材料状态
|
|
|||
|
资料 1
|
||||
|
UL 黄卡 2
|
||||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
特性
|
|
|||
|
用途
|
|
|||
|
外观
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.19
|
g/cm3
|
ASTM D792, ISO 1183 |
|
熔流率（熔体流动速率） (300°C/1.2 kg)
|
20
|
g/10 min
|
ASTM D1238 |
|
溶化体积流率（MVR） (300°C/1.2 kg)
|
19.0
|
cm3/10min
|
ISO 1133 |
|
收缩率
|
内部方法 | ||
|
流动 : 3.20 mm
|
0.40 到 0.80
|
%
|
|
|
横向流动 : 3.20 mm
|
0.40 到 0.80
|
%
|
|
|
吸水率
|
ISO 62 | ||
|
饱和, 23°C
|
0.12
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.090
|
%
|
|
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
洛氏硬度 (L 计秤)
|
89
|
|
ISO 2039-2 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
-- 3
|
2260
|
MPa
|
ASTM D638 |
|
--
|
2340
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服 4
|
58.6
|
MPa
|
ASTM D638 |
|
屈服
|
57.8
|
MPa
|
ISO 527-2/50 |
|
断裂 4
|
57.1
|
MPa
|
ASTM D638 |
|
断裂
|
56.8
|
MPa
|
ISO 527-2/50 |
|
伸长率
|
|||
|
屈服 4
|
5.7
|
%
|
ASTM D638 |
|
屈服
|
5.4
|
%
|
ISO 527-2/50 |
|
断裂 4
|
120
|
%
|
ASTM D638 |
|
断裂
|
120
|
%
|
ISO 527-2/50 |
|
弯曲模量
|
|||
|
50.0 mm 跨距 5
|
2250
|
MPa
|
ASTM D790 |
|
-- 6
|
2150
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
-- 6, 7
|
89.5
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距 5
|
94.8
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度 8
|
ISO 179/1eA | ||
|
-30°C
|
45
|
kJ/m2
|
|
|
23°C
|
65
|
kJ/m2
|
|
|
简支梁无缺口冲击强度 8
|
ISO 179/1eU | ||
|
-30°C
|
无断裂
|
|
|
|
23°C
|
无断裂
|
|
|
|
悬壁梁缺口冲击强度
|
|||
|
-30°C
|
620
|
J/m
|
ASTM D256 |
|
23°C
|
740
|
J/m
|
ASTM D256 |
|
-30°C 9
|
55
|
kJ/m2
|
ISO 180/1A |
|
23°C 9
|
65
|
kJ/m2
|
ISO 180/1A |
|
无缺口伊佐德冲击强度 9
|
ISO 180/1U | ||
|
-30°C
|
无断裂
|
|
|
|
23°C
|
无断裂
|
|
|
|
装有测量仪表的落镖冲击 (23°C, Total Energy)
|
74.9
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
1.8 MPa, 未退火, 3.20 mm
|
122
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 64.0 mm 跨距 10
|
117
|
°C
|
ISO 75-2/Af |
|
维卡软化温度
|
|||
|
--
|
139
|
°C
|
ASTM D1525 11, ISO 306/B50 11 |
|
--
|
140
|
°C
|
ISO 306/B120 |
|
Ball Pressure Test (125°C)
|
Pass
|
|
IEC 60695-10-2 |
|
线形热膨胀系数
|
|||
|
流动 : -40 到 95°C
|
7.5E-5
|
cm/cm/°C
|
ASTM E831 |
|
流动 : 23 到 80°C
|
7.5E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
横向 : -40 到 95°C
|
7.6E-5
|
cm/cm/°C
|
ASTM E831 |
|
横向 : 23 到 80°C
|
7.6E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
RTI Elec
|
130
|
°C
|
UL 746 |
|
RTI
|
130
|
°C
|
UL 746 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
> 1.0E+15
|
ohm
|
ASTM D257 |
|
体积电阻率
|
> 1.0E+15
|
ohm·cm
|
ASTM D257 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级 (1.50 mm)
|
HB
|
|
UL 94 |
|
灼热丝易燃指数 (3.00 mm)
|
960
|
°C
|
IEC 60695-2-12 |
|
热灯丝点火温度
|
IEC 60695-2-13 | ||
|
0.800 mm
|
850
|
°C
|
|
|
3.00 mm
|
850
|
°C
|
| 光学性能 |
额定值
|
单位制
|
测试方法
|
|
透射率 (2540 μm)
|
82.0
|
%
|
ASTM D1003 |
|
雾度 (2540 μm)
|
3.0
|
%
|
ASTM D1003 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
121
|
°C
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
干燥时间，最大
|
48
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 60
|
%
|
|
|
料筒后部温度
|
217 到 293
|
°C
|
|
|
料筒中部温度
|
282 到 304
|
°C
|
|
|
料筒前部温度
|
293 到 316
|
°C
|
|
|
射嘴温度
|
288 到 310
|
°C
|
|
|
加工（熔体）温度
|
293 到 316
|
°C
|
|
|
模具温度
|
71.1 到 93.3
|
°C
|
|
|
背压
|
0.345 到 0.689
|
MPa
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
0.025 到 0.076
|
mm
|
| 备注 |
 |