LNP? STAT-KON? DX04489C compound
聚碳酸酯
专有填料
产品说明:
LNP STAT-KON* DX04489C is a high modulus compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive.
Also known as: LNP* STAT-KON* Compound PDX-D-04489 CCS
Product reorder name: DX04489C
Also known as: LNP* STAT-KON* Compound PDX-D-04489 CCS
Product reorder name: DX04489C
| 总体 | |
|
材料状态
|
|
|
资料1
|
|
|
UL 黄卡2
|
|
|
搜索 UL 黄卡
|
|
|
供货地区
|
|
|
填料/增强材料
|
|
|
特性
|
Low (to None) Ion Content导电 |
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.33
|
g/cm3
|
ASTM D792 |
|
收缩率 - 横向流动(24小时)
|
0.30
|
%
|
ASTM D955 |
|
吸水率(24 hr, 50% RH)
|
0.10
|
%
|
ASTM D570 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量3
|
16600
|
MPa
|
ASTM D638 |
|
抗张强度
|
ASTM D638 | ||
|
屈服
|
130
|
MPa
|
|
|
断裂
|
111
|
MPa
|
|
|
伸长率
|
ASTM D638 | ||
|
屈服
|
2.2
|
%
|
|
|
断裂
|
2.4
|
%
|
|
|
弯曲模量
|
15500
|
MPa
|
ASTM D790 |
|
弯曲强度
|
207
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度(23°C)
|
59
|
J/m
|
ASTM D256 |
|
无缺口悬臂梁冲击(23°C)
|
480
|
J/m
|
ASTM D4812 |
|
装有测量仪表的落镖冲击(23°C, Energy at Peak Load)
|
11.5
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度(1.8 MPa, 未退火, 3.20 mm)
|
140
|
°C
|
ASTM D648 |
|
线形热膨胀系数
|
ASTM E831 | ||
|
流动 : -40 到 40°C
|
1.6E-5
|
cm/cm/°C
|
|
|
横向 : -40 到 40°C
|
4.1E-5
|
cm/cm/°C
|
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
1.0E 2 到 1.0E 6
|
ohm
|
ASTM D257 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
121
|
°C
|
|
|
干燥时间
|
4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
料筒后部温度
|
293 到 304
|
°C
|
|
|
料筒中部温度
|
310 到 321
|
°C
|
|
|
料筒前部温度
|
321 到 332
|
°C
|
|
|
加工（熔体）温度
|
304 到 327
|
°C
|
|
|
模具温度
|
82.2 到 110
|
°C
|
|
|
背压
|
0.172 到 0.344
|
MPa
|
|
|
螺杆转速
|
30 到 60
|
rpm
|
备注  |