上海沐音新材料有限公司
LNP? STAT-KON? DX03571 compound
聚碳酸酯
产品说明:
LNP STAT-KON DX03571 is a compound based on Polycarbonate resin. Added features of this material include: Electrically Conductive.
Also known as: LNP* STAT-KON* Compound PDX-D-03571
Product reorder name: DX03571
Also known as: LNP* STAT-KON* Compound PDX-D-03571
Product reorder name: DX03571
| 总体 | |
|
材料状态
|
|
|
资料 1
|
|
|
搜索 UL 黄卡
|
|
|
供货地区
|
|
|
特性
|
|
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.26
|
g/cm3
|
ASTM D792 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量 2
|
2900
|
MPa
|
ASTM D638 |
|
抗张强度
|
ASTM D638 | ||
|
断裂
|
60.7
|
MPa
|
|
|
断裂 3
|
60.7
|
MPa
|
|
|
伸长率
|
ASTM D638 | ||
|
断裂
|
4.0
|
%
|
|
|
断裂 3
|
4.0
|
%
|
|
|
弯曲模量
|
ASTM D790 | ||
|
--
|
2830
|
MPa
|
|
|
50.0 mm 跨距 4
|
2830
|
MPa
|
|
|
弯曲强度
|
ASTM D790 | ||
|
--
|
96.5
|
MPa
|
|
|
断裂, 50.0 mm 跨距 4
|
96.5
|
MPa
|
|
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度 (23°C)
|
53
|
J/m
|
ASTM D256 |
|
无缺口悬臂梁冲击 (23°C)
|
1100
|
J/m
|
ASTM D4812 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度 (1.8 MPa, 未退火, 3.20 mm)
|
121
|
°C
|
ASTM D648 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
1.0E+2 到 1.0E+4
|
ohm
|
ASTM D257 |
|
体积电阻率
|
1.0E+2 到 1.0E+4
|
ohm·cm
|
ASTM D257 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
121
|
°C
|
|
|
干燥时间
|
4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
料筒后部温度
|
293 到 304
|
°C
|
|
|
料筒中部温度
|
310 到 321
|
°C
|
|
|
料筒前部温度
|
321 到 332
|
°C
|
|
|
加工（熔体）温度
|
304 到 327
|
°C
|
|
|
模具温度
|
82.2 到 110
|
°C
|
|
|
背压
|
0.172 到 0.344
|
MPa
|
|
|
螺杆转速
|
30 到 60
|
rpm
|
备注  |