上海沐音新材料有限公司
LNP? LUBRICOMP? DFL28EG compound
聚碳酸酯
40% 玻璃纤维增强材料
产品说明:
LNP LUBRICOMP DFL28EG is a compound based on Polycarbonate resin containing 40% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated, Easy Molding.
Also known as: LNP* LUBRICOMP* Compound DFL-4028 EM MG
Product reorder name: DFL28EG
Also known as: LNP* LUBRICOMP* Compound DFL-4028 EM MG
Product reorder name: DFL28EG
| 总体 | |
|
材料状态
|
|
|
资料1
|
|
|
搜索 UL 黄卡
|
|
|
供货地区
|
|
|
填料/增强材料
|
|
|
添加剂
|
|
|
特性
|
良好的成型性能润滑 |
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
ASTM D792 | ||
|
--
|
1.62
|
g/cm3
|
|
|
--
|
1.61
|
g/cm3
|
|
|
收缩率 - 横向流动(24小时)
|
0.30 到 0.60
|
%
|
ASTM D955 |
|
吸水率
|
|||
|
24 hr, 50% RH
|
0.080
|
%
|
ASTM D570 |
|
平衡, 23°C, 50% RH
|
0.12
|
%
|
ISO 62 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
--2
|
11000
|
MPa
|
ASTM D638 |
|
--
|
10200
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服3
|
115
|
MPa
|
ASTM D638 |
|
屈服
|
116
|
MPa
|
ISO 527-2/5 |
|
断裂3
|
115
|
MPa
|
ASTM D638 |
|
断裂
|
116
|
MPa
|
ISO 527-2/5 |
|
伸长率
|
|||
|
屈服3
|
1.9
|
%
|
ASTM D638 |
|
屈服
|
1.9
|
%
|
ISO 527-2/5 |
|
断裂
|
0.0
|
%
|
ASTM D638 |
|
断裂3
|
1.9
|
%
|
ASTM D638 |
|
断裂
|
2.0
|
%
|
ISO 527-2/5 |
|
弯曲模量
|
|||
|
50.0 mm 跨距4
|
9860
|
MPa
|
ASTM D790 |
|
--5
|
9780
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
--
|
174
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距4
|
176
|
MPa
|
ASTM D790 |
|
断裂, 50.0 mm 跨距4
|
176
|
MPa
|
ASTM D790 |
|
摩擦系数
|
ASTM D3702 Modified | ||
|
与自身 - 动态
|
0.61
|
|
|
|
与自身 - 静态
|
0.58
|
|
|
|
磨损因数
|
ASTM D3702 Modified | ||
|
Ring
|
2.60
|
10^-10 in^5-min/ft-lb-hr
|
|
|
Washer
|
45.0
|
10^-10 in^5-min/ft-lb-hr
|
|
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度
|
|||
|
23°C
|
130
|
J/m
|
ASTM D256 |
|
23°C6
|
12
|
kJ/m2
|
ISO 180/1A |
|
无缺口悬臂梁冲击
|
|||
|
23°C
|
650
|
J/m
|
ASTM D4812 |
|
23°C6
|
41
|
kJ/m2
|
ISO 180/1U |
|
装有测量仪表的落镖冲击
|
|||
|
23°C, Total Energy
|
19.9
|
J
|
ASTM D3763 |
|
--
|
4.80
|
J
|
ISO 6603-2 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
0.45 MPa, 未退火, 3.20 mm
|
141
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 64.0 mm 跨距7
|
141
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, 未退火, 3.20 mm
|
140
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 64.0 mm 跨距7
|
139
|
°C
|
ISO 75-2/Af |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
121
|
°C
|
|
|
干燥时间
|
4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
料筒后部温度
|
293 到 304
|
°C
|
|
|
料筒中部温度
|
310 到 321
|
°C
|
|
|
料筒前部温度
|
321 到 332
|
°C
|
|
|
加工（熔体）温度
|
304 到 327
|
°C
|
|
|
模具温度
|
82.2 到 110
|
°C
|
|
|
背压
|
0.172 到 0.344
|
MPa
|
|
|
螺杆转速
|
30 到 60
|
rpm
|
备注  |