上海沐音新材料有限公司
LNP? THERMOCOMP? DF006LXN compound
聚碳酸酯
30% 玻璃纤维增强材料
产品说明:
LNP THERMOCOMP DF006LXN is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material are: Low Extractable, NSF Listed.
Also known as: LNP* THERMOCOMP* Compound DF006LXN
Product reorder name: DF006LXN
Also known as: LNP* THERMOCOMP* Compound DF006LXN
Product reorder name: DF006LXN
| 总体 | |
|
材料状态
|
|
|
资料 1
|
|
|
搜索 UL 黄卡
|
|
|
供货地区
|
|
|
填料/增强材料
|
|
|
特性
|
|
|
机构评级
|
|
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.45
|
g/cm3
|
ASTM D792, ISO 1183 |
|
吸水率
|
|||
|
24 hr, 50% RH
|
0.070
|
%
|
ASTM D570 |
|
平衡, 23°C, 50% RH
|
0.070
|
%
|
ISO 62 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量 2
|
8640
|
MPa
|
ASTM D638 |
|
抗张强度
|
|||
|
断裂 3
|
114
|
MPa
|
ASTM D638 |
|
断裂
|
114
|
MPa
|
ISO 527-2/5 |
|
伸长率
|
|||
|
屈服 3
|
2.7
|
%
|
ASTM D638 |
|
断裂 3
|
3.2
|
%
|
ASTM D638 |
|
断裂
|
7.5
|
%
|
ISO 527-2/5 |
|
弯曲模量
|
|||
|
50.0 mm 跨距 4
|
8230
|
MPa
|
ASTM D790 |
|
-- 5
|
7870
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
--
|
185
|
MPa
|
ISO 178 |
|
断裂, 50.0 mm 跨距 4
|
149
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度
|
|||
|
23°C
|
140
|
J/m
|
ASTM D256 |
|
23°C 6
|
14
|
kJ/m2
|
ISO 180/1A |
|
无缺口悬臂梁冲击
|
|||
|
23°C
|
910
|
J/m
|
ASTM D4812 |
|
23°C 6
|
57
|
kJ/m2
|
ISO 180/1U |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
0.45 MPa, 未退火, 3.20 mm
|
144
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 64.0 mm 跨距 7
|
145
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, 未退火, 3.20 mm
|
140
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 64.0 mm 跨距 7
|
141
|
°C
|
ISO 75-2/Af |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
121
|
°C
|
|
|
干燥时间
|
4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
料筒后部温度
|
293 到 304
|
°C
|
|
|
料筒中部温度
|
310 到 321
|
°C
|
|
|
料筒前部温度
|
321 到 332
|
°C
|
|
|
加工（熔体）温度
|
304 到 327
|
°C
|
|
|
模具温度
|
82.2 到 110
|
°C
|
|
|
背压
|
0.172 到 0.344
|
MPa
|
|
|
螺杆转速
|
30 到 60
|
rpm
|
备注  |