上海沐音新材料有限公司
LEXAN? BPL1000 resin
聚碳酸酯
产品说明:
LEXAN BPL1000 Polycarbonate (PC) resin is an injection moldable grade featuring high flow and good impact peroformance. It contains non-chlorinated and non-brominated flame retardant systems with UL-94 V0 rating at 0.8mm. LEXAN BPL1000 resin offers various opaque color options and is ideal for thin wall applications.
| 总体 | ||||
|
材料状态
|
|
|||
|
资料 1
|
||||
|
UL 黄卡 2
|
||||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
添加剂
|
|
|||
|
特性
|
|
|||
|
用途
|
|
|||
|
外观
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
|||
|
--
|
1.17
|
g/cm3
|
ASTM D792 |
|
--
|
1.20
|
g/cm3
|
ISO 1183 |
|
熔流率（熔体流动速率） (300°C/1.2 kg)
|
25
|
g/10 min
|
ASTM D1238 |
|
溶化体积流率（MVR） (300°C/1.2 kg)
|
23.2
|
cm3/10min
|
ISO 1133 |
|
收缩率
|
内部方法 | ||
|
流动 3
|
0.50 到 0.70
|
%
|
|
|
流动 : 3.20 mm
|
0.50 到 0.70
|
%
|
|
|
横向流动 : 3.20 mm
|
0.50 到 0.70
|
%
|
|
|
吸水率
|
|||
|
24 hr
|
0.15
|
%
|
ASTM D570 |
|
饱和, 23°C
|
0.35
|
%
|
ISO 62 |
|
平衡, 23°C, 50% RH
|
0.15
|
%
|
ISO 62 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
-- 4
|
2680
|
MPa
|
ASTM D638 |
|
--
|
2460
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服
|
58.8
|
MPa
|
内部方法 |
|
屈服 5
|
63.4
|
MPa
|
ASTM D638 |
|
屈服
|
64.8
|
MPa
|
ISO 527-2/50 |
|
断裂 5
|
51.0
|
MPa
|
ASTM D638 |
|
断裂
|
53.5
|
MPa
|
ISO 527-2/50 |
|
伸长率
|
|||
|
屈服 5
|
4.8
|
%
|
ASTM D638 |
|
屈服
|
4.7
|
%
|
ISO 527-2/50 |
|
断裂
|
100
|
%
|
内部方法 |
|
断裂 5
|
96
|
%
|
ASTM D638 |
|
断裂
|
97
|
%
|
ISO 527-2/50 |
|
弯曲模量
|
|||
|
50.0 mm 跨距 6
|
2670
|
MPa
|
ASTM D790 |
|
--
|
2200
|
MPa
|
ASTM D790 |
|
-- 7
|
2370
|
MPa
|
ISO 178 |
|
弯曲强度
|
|||
|
--
|
93.2
|
MPa
|
ASTM D790 |
|
-- 7, 8
|
94.8
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距 6
|
102
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度 9 (23°C)
|
18
|
kJ/m2
|
ISO 179/1eA |
|
悬壁梁缺口冲击强度
|
|||
|
23°C
|
600
|
J/m
|
ASTM D256 |
|
-30°C 10
|
12
|
kJ/m2
|
ISO 180/1A |
|
23°C 10
|
18
|
kJ/m2
|
ISO 180/1A |
|
装有测量仪表的落镖冲击 (23°C, Total Energy)
|
48.6
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
0.45 MPa, 未退火, 3.20 mm
|
106
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 64.0 mm 跨距 11
|
96.1
|
°C
|
ISO 75-2/Af |
|
维卡软化温度
|
|||
|
--
|
111
|
°C
|
ASTM D1525 12 |
|
--
|
113
|
°C
|
ISO 306/B50 |
|
--
|
114
|
°C
|
ISO 306/B120 |
|
Ball Pressure Test (75°C)
|
Pass
|
|
IEC 60695-10-2 |
|
线形热膨胀系数
|
|||
|
流动 : -40 到 40°C
|
7.0E-5
|
cm/cm/°C
|
ASTM E831, ISO 11359-2 |
|
流动 : -30 到 30°C
|
7.0E-5
|
cm/cm/°C
|
ASTM E831 |
|
横向 : -40 到 40°C
|
7.0E-5
|
cm/cm/°C
|
ASTM E831, ISO 11359-2 |
|
RTI Elec
|
80.0
|
°C
|
UL 746 |
|
RTI Imp
|
80.0
|
°C
|
UL 746 |
|
RTI
|
80.0
|
°C
|
UL 746 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
> 1.0E+15
|
ohm
|
IEC 60093 |
|
体积电阻率
|
> 1.0E+15
|
ohm·cm
|
IEC 60093 |
|
介电强度 (1.60 mm, in Oil)
|
27
|
kV/mm
|
ASTM D149 |
|
相对电容率
|
IEC 60250 | ||
|
50 Hz
|
3.00
|
|
|
|
60 Hz
|
3.00
|
|
|
|
1 MHz
|
2.90
|
|
|
|
耗散因数
|
IEC 60250 | ||
|
50 Hz
|
0.030
|
|
|
|
60 Hz
|
0.030
|
|
|
|
1 MHz
|
0.010
|
|
|
|
漏电起痕指数
|
200
|
V
|
IEC 60112 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级
|
UL 94 | ||
|
0.450 mm
|
V-2
|
|
|
|
0.800 mm
|
V-0
|
|
|
|
灼热丝易燃指数 (1.00 mm)
|
960
|
°C
|
IEC 60695-2-12 |
|
热灯丝点火温度 (1.00 mm)
|
800
|
°C
|
IEC 60695-2-13 |
|
极限氧指数
|
36
|
%
|
ISO 4589-2 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
90.0
|
°C
|
|
|
干燥时间
|
4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
料斗温度
|
60.0 到 80.0
|
°C
|
|
|
料筒后部温度
|
260 到 280
|
°C
|
|
|
料筒中部温度
|
270 到 290
|
°C
|
|
|
料筒前部温度
|
280 到 300
|
°C
|
|
|
射嘴温度
|
270 到 290
|
°C
|
|
|
加工（熔体）温度
|
280 到 300
|
°C
|
|
|
模具温度
|
90.0
|
°C
|
备注  |