上海沐音新材料有限公司
LNP? STAT-KON? 9X02785 compound
聚碳酸酯
专有填料
产品说明:
LNP STAT-KON* 9X02785 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive.
Also known as: LNP* STAT-KON* Compound PDX-D-02785
Product reorder name: 9X02785
Also known as: LNP* STAT-KON* Compound PDX-D-02785
Product reorder name: 9X02785
| 总体 | |
|
材料状态
|
|
|
资料 1
|
|
|
搜索 UL 黄卡
|
|
|
供货地区
|
|
|
填料/增强材料
|
|
|
特性
|
|
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
ASTM D792 | ||
|
--
|
1.27
|
g/cm3
|
|
|
--
|
1.26
|
g/cm3
|
|
|
收缩率
|
ASTM D955 | ||
|
流动 : 24小时
|
0.40 到 0.70
|
%
|
|
|
横向流动 : 24小时
|
0.50 到 0.80
|
%
|
|
|
吸水率
|
|||
|
24 hr, 50% RH
|
0.091
|
%
|
ASTM D570 |
|
平衡, 23°C, 50% RH
|
0.14
|
%
|
ISO 62 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
-- 2
|
2850
|
MPa
|
ASTM D638 |
|
--
|
2760
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服
|
64.1
|
MPa
|
ASTM D638 |
|
屈服 3
|
63.0
|
MPa
|
ASTM D638 |
|
屈服
|
56.0
|
MPa
|
ISO 527-2/5 |
|
断裂 3
|
52.0
|
MPa
|
ASTM D638 |
|
断裂
|
52.0
|
MPa
|
ISO 527-2/5 |
|
伸长率
|
|||
|
屈服 3
|
4.3
|
%
|
ASTM D638 |
|
屈服
|
2.9
|
%
|
ISO 527-2/5 |
|
断裂
|
4.0
|
%
|
ASTM D638 |
|
断裂 3
|
7.8
|
%
|
ASTM D638 |
|
断裂
|
3.1
|
%
|
ISO 527-2/5 |
|
弯曲模量
|
|||
|
50.0 mm 跨距 4
|
2920
|
MPa
|
ASTM D790 |
|
--
|
2900
|
MPa
|
ASTM D790 |
|
-- 5
|
2800
|
MPa
|
ISO 178 |
|
弯曲强度
|
|||
|
--
|
103
|
MPa
|
ASTM D790 |
|
--
|
96.0
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距 4
|
107
|
MPa
|
ASTM D790 |
|
断裂, 50.0 mm 跨距 4
|
75.9
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度
|
|||
|
23°C
|
60
|
J/m
|
ASTM D256 |
|
23°C 6
|
7.1
|
kJ/m2
|
ISO 180/1A |
|
无缺口悬臂梁冲击
|
|||
|
23°C
|
2200
|
J/m
|
ASTM D4812 |
|
23°C 6
|
150
|
kJ/m2
|
ISO 180/1U |
|
装有测量仪表的落镖冲击
|
|||
|
23°C, Total Energy
|
35.7
|
J
|
ASTM D3763 |
|
--
|
35.4
|
J
|
ISO 6603-2 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
0.45 MPa, 未退火, 3.20 mm
|
117
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 64.0 mm 跨距 7
|
114
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, 未退火, 3.20 mm
|
106
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 64.0 mm 跨距 7
|
103
|
°C
|
ISO 75-2/Af |
|
线形热膨胀系数
|
ASTM D696 | ||
|
流动 : -30 到 30°C
|
6.8E-5
|
cm/cm/°C
|
|
|
横向 : -30 到 30°C
|
6.8E-5
|
cm/cm/°C
|
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
1.0E+2 到 1.0E+5
|
ohm
|
ASTM D257 |
|
体积电阻率
|
1.0E+2 到 1.0E+7
|
ohm·cm
|
ASTM D257 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
121
|
°C
|
|
|
干燥时间
|
4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
料筒后部温度
|
293 到 304
|
°C
|
|
|
料筒中部温度
|
310 到 321
|
°C
|
|
|
料筒前部温度
|
321 到 332
|
°C
|
|
|
加工（熔体）温度
|
304 到 327
|
°C
|
|
|
模具温度
|
82.2 到 110
|
°C
|
|
|
背压
|
0.172 到 0.344
|
MPa
|
|
|
螺杆转速
|
30 到 60
|
rpm
|
备注  |