上海沐音新材料有限公司
|
Ultraform? S 2320 003 UNC Q600
聚甲醛（POM）共聚物
BASF CorporationWeb
|
| 产品说明 | |
|
Ultraform S 2320 003 UNC Q600 is an easy flowing and rapidly freezing injection molding POM grade. Contains a mold release agent.
|
|
| 总体 | |
|
材料状态
|
|
|
资料1
|
Processing - Injection Molding Cooling Times (English)Technical Datasheet - ASTM (English)Technical Datasheet - ISO (English) |
|
UL 黄卡2
|
|
|
搜索 UL 黄卡
|
BASF CorporationUltraform? |
|
供货地区
|
|
|
添加剂
|
|
|
性能特点
|
|
|
用途
|
|
|
机构评级
|
EC 1907/2006 (REACH)FDA 21 CFR 177.2470 |
|
RoHS 合规性
|
|
|
外观
|
|
|
形式
|
|
|
加工方法
|
|
|
多点数据
|
Isochronous Stress vs. Strain (ISO 11403-1)Isothermal Stress vs. Strain (ISO 11403-1)Secant Modulus vs. Strain (ISO 11403-1)Shear Modulus vs. Temperature (ISO 11403-1)Specific Heat vs. Temperature (ISO 11403-2)Specific Volume vs Temperature (ISO 11403-2)Viscosity vs. Shear Rate (ISO 11403-2) |
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
|||
|
--
|
1.40
|
g/cm3
|
ASTM D792 |
|
--
|
1400
|
kg/m3
|
ISO 11833 |
|
熔体体积流动速率(190°C/2.16 kg)
|
11.0
|
cm3/10min
|
ISO 11333 |
|
收缩率
|
|||
|
流动: 3.18 mm
|
2.0
|
%
|
ASTM D955 |
|
横向流量
|
2.1
|
%
|
ISO 294-4 |
|
流量
|
2.1
|
%
|
ISO 294-4 |
|
吸水率
|
|||
|
饱和
|
0.80
|
%
|
ASTM D570,ISO 623 |
|
平衡, 50% RH
|
0.20
|
%
|
ASTM D570 |
|
平衡
|
0.20
|
%
|
ISO 623 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
2700
|
MPa
|
ISO 527-23 |
|
抗张强度
|
|||
|
屈服, 23°C
|
65.0
|
MPa
|
ASTM D638 |
|
屈服, -40°C
|
93.0
|
MPa
|
ISO 527-2 |
|
屈服, 80°C
|
33.0
|
MPa
|
ISO 527-2 |
|
屈服
|
65.0
|
MPa
|
ISO 527-23 |
|
伸长率
|
|||
|
屈服, 23°C
|
9.0
|
%
|
ASTM D638 |
|
屈服
|
9.0
|
%
|
ISO 527-23 |
|
断裂伸长率
|
28
|
%
|
ISO 527-23 |
|
拉伸蠕变模量
|
ISO 899-13 | ||
|
1 hr
|
1900
|
MPa
|
|
|
1000 hr
|
1300
|
MPa
|
|
|
弯曲模量(23°C)
|
2620
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度
|
ISO 179/1eA3 | ||
|
-30°C
|
5.00
|
kJ/m2
|
|
|
23°C
|
5.50
|
kJ/m2
|
|
|
简支梁缺口冲击强度
|
ISO 179 | ||
|
-30°C
|
170
|
kJ/m2
|
|
|
23°C
|
180
|
kJ/m2
|
|
|
悬壁梁缺口冲击强度
|
ASTM D256 | ||
|
-40°C
|
50
|
J/m
|
|
|
23°C
|
60
|
J/m
|
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
热变形温度
|
|||
|
0.45 MPa, 未退火
|
160
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火
|
110
|
°C
|
ASTM D648 |
|
1.8 MPa
|
100
|
°C
|
ISO 75-23 |
|
熔融峰值温度
|
167
|
°C
|
ASTM D3418,ISO 3146 |
|
线形膨胀系数 - 流动
|
|||
|
--
|
0.000060
|
cm/cm/°C
|
ASTM E831 |
|
--
|
0.00011
|
cm/cm/°C
|
ISO 11359-2 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率4
|
1.0E 13
|
ohm
|
ASTM D2573,IEC 600933 |
|
体积电阻率
|
|||
|
1.50 mm
|
1.0E 13
|
ohm·cm
|
ASTM D257 |
|
--
|
1.0E 11
|
ohm·m
|
IEC 600933 |
|
耐电强度
|
40
|
kV/mm
|
IEC 60243-13 |
|
相对电容率
|
IEC 602503 | ||
|
100 Hz
|
3.80
|
|
|
|
1 MHz
|
3.80
|
|
|
|
耗散因数
|
IEC 602503 | ||
|
100 Hz
|
0.0010
|
|
|
|
1 MHz
|
0.0050
|
|
|
|
漏电起痕指数
|
600
|
|
IEC 601123 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
80.0 到 110
|
°C
|
|
|
干燥时间
|
2.0 到 4.0
|
hr
|
|
|
建议的最大水分含量
|
0.15
|
%
|
|
|
加工（熔体）温度
|
190 到 230
|
°C
|
|
|
模具温度
|
60.0 到 120
|
°C
|
|
|
注塑温度
|
3.50 到 7.00
|
MPa
|
|
|
注射速度
|
快速
|
|
备注  |