上海沐音新材料有限公司
Ultraform? S 1320 0021 UNC
聚甲醛（POM）共聚物
BASF Corporation Web
| 产品说明 | ||||
|
Ultraform S 1320 0021 UNC is an easy flowing, rapidly freezing injection molding POM grade with enhanced stiffness and heat distortion resistance. It is highly stabilized to resist aggressive fuels, including hot diesel fuel.
|
||||
| 总体 | ||||
|
材料状态
|
|
|||
|
资料 1
|
|
|||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
性能特点
|
|
|||
|
用途
|
|
|||
|
机构评级
|
|
|||
|
RoHS 合规性
|
|
|||
|
外观
|
|
|||
|
形式
|
|
|||
|
加工方法
|
|
|||
|
多点数据
|
|
|||
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
密度
|
1410
|
kg/m3
|
ISO 1183 2 |
|
熔体体积流动速率 (190°C/2.16 kg)
|
11.0
|
cm3/10min
|
ISO 1133 2 |
|
收缩率
|
ISO 294-4 | ||
|
横向流量
|
2.1
|
%
|
|
|
流量
|
2.1
|
%
|
|
|
吸水率
|
ISO 62 2 | ||
|
饱和
|
0.80
|
%
|
|
|
平衡
|
0.20
|
%
|
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
3000
|
MPa
|
ISO 527-2 2 |
|
拉伸应力
|
|||
|
屈服, -40°C
|
97.0
|
MPa
|
ISO 527-2 |
|
屈服, 80°C
|
35.0
|
MPa
|
ISO 527-2 |
|
屈服
|
66.0
|
MPa
|
ISO 527-2 2 |
|
拉伸应变 (屈服)
|
9.0
|
%
|
ISO 527-2 2 |
|
断裂伸长率
|
30
|
%
|
ISO 527-2 2 |
|
拉伸蠕变模量 (1000 hr)
|
1450
|
MPa
|
ISO 899-1 2 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度
|
ISO 179/1eA 2 | ||
|
-30°C
|
5.50
|
kJ/m2
|
|
|
23°C
|
5.50
|
kJ/m2
|
|
|
简支梁缺口冲击强度
|
ISO 179 | ||
|
-30°C
|
170
|
kJ/m2
|
|
|
23°C
|
170
|
kJ/m2
|
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
热变形温度 (1.8 MPa)
|
100
|
°C
|
ISO 75-2 2 |
|
溶融温度（DSC）
|
171
|
°C
|
ISO 3146 |
|
线形膨胀系数 - 流动
|
0.00011
|
cm/cm/°C
|
ISO 11359-2 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
1.0E+15
|
ohm
|
IEC 60093 2 |
|
体积电阻率
|
1.0E+10
|
ohm·m
|
IEC 60093 2 |
|
耐电强度
|
40
|
kV/mm
|
IEC 60243-1 2 |
|
相对电容率
|
IEC 60250 2 | ||
|
100 Hz
|
3.70
|
|
|
|
1 MHz
|
3.70
|
|
|
|
耗散因数
|
IEC 60250 2 | ||
|
100 Hz
|
0.0020
|
|
|
|
1 MHz
|
0.0050
|
|
|
|
漏电起痕指数
|
600
|
|
IEC 60112 2 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
80.0 到 110
|
°C
|
|
|
干燥时间
|
2.0 到 4.0
|
hr
|
|
|
建议的最大水分含量
|
0.15
|
%
|
|
|
加工（熔体）温度
|
190 到 230
|
°C
|
|
|
模具温度
|
60.0 到 120
|
°C
|
|
|
注塑温度
|
3.50 到 7.00
|
MPa
|
|
|
注射速度
|
快速
|
|
备注  |