上海沐音新材料有限公司
LEXAN? 104R resin
聚碳酸酯
产品说明:
LEXAN 104R is a high viscosity multi purpose grade. FDA food contact compliant in limited colors. Effective January 15th, 2007 this grade is no longer supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Contact your GE representative for the alternative grade in the LEXAN HP series.
| 总体 | |
|
材料状态
|
|
|
资料1
|
|
|
UL 黄卡2
|
|
|
搜索 UL 黄卡
|
SABIC Innovative Plastics Asia PacificLEXAN? |
|
供货地区
|
|
|
特性
|
食品接触的合规性通用粘度，高 |
|
用途
|
|
|
机构评级
|
|
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
ASTM D792 | ||
|
--
|
1.20
|
g/cm3
|
|
|
--
|
1.19
|
g/cm3
|
|
|
特定体积
|
0.835
|
cm3/g
|
ASTM D792 |
|
熔流率（熔体流动速率）(300°C/1.2 kg)
|
7.0
|
g/10 min
|
ASTM D1238 |
|
收缩率 - 流动(3.20 mm)
|
0.50 到 0.70
|
%
|
内部方法 |
|
吸水率
|
ASTM D570 | ||
|
24 hr
|
0.15
|
%
|
|
|
平衡, 23°C
|
0.35
|
%
|
|
|
平衡, 100°C
|
0.58
|
%
|
|
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
洛氏硬度
|
ASTM D785 | ||
|
M 级
|
70
|
|
|
|
R 级
|
118
|
|
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
抗张强度3
|
ASTM D638 | ||
|
屈服
|
62.1
|
MPa
|
|
|
断裂
|
68.9
|
MPa
|
|
|
伸长率3
|
ASTM D638 | ||
|
屈服
|
7.0
|
%
|
|
|
断裂
|
140
|
%
|
|
|
弯曲模量4(50.0 mm 跨距)
|
2340
|
MPa
|
ASTM D790 |
|
弯曲强度4(屈服, 50.0 mm 跨距)
|
97.9
|
MPa
|
ASTM D790 |
|
泰伯耐磨性(1000 Cycles, 1000 g, CS-17 转轮)
|
10.0
|
mg
|
ASTM D1044 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度(23°C)
|
910
|
J/m
|
ASTM D256 |
|
无缺口悬臂梁冲击(23°C)
|
3200
|
J/m
|
ASTM D4812 |
|
落锤冲击(23°C)
|
169
|
J
|
ASTM D3029 |
|
拉伸冲击强度5
|
630
|
kJ/m2
|
ASTM D1822 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
ASTM D648 | ||
|
0.45 MPa, 未退火, 6.40 mm
|
138
|
°C
|
|
|
1.8 MPa, 未退火, 6.40 mm
|
132
|
°C
|
|
|
维卡软化温度
|
154
|
°C
|
ASTM D15256 |
|
线形热膨胀系数 - 流动(-40 到 95°C)
|
6.8E-5
|
cm/cm/°C
|
ASTM E831 |
|
比热
|
1260
|
J/kg/°C
|
ASTM C351 |
|
导热系数
|
0.19
|
W/m/K
|
ASTM C177 |
|
RTI Elec
|
130
|
°C
|
UL 746 |
|
RTI Imp
|
130
|
°C
|
UL 746 |
|
RTI
|
130
|
°C
|
UL 746 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
体积电阻率
|
1.0E 17
|
ohm·cm
|
ASTM D257 |
|
介电强度(3.20 mm, in Air)
|
15
|
kV/mm
|
ASTM D149 |
|
介电常数
|
ASTM D150 | ||
|
50 Hz
|
3.17
|
|
|
|
60 Hz
|
3.17
|
|
|
|
1 MHz
|
2.96
|
|
|
|
耗散因数
|
ASTM D150 | ||
|
50 Hz
|
9.0E-4
|
|
|
|
60 Hz
|
9.0E-4
|
|
|
|
1 MHz
|
0.010
|
|
|
|
相比耐漏电起痕指数(CTI)
|
PLC 2
|
|
UL 746 |
|
高电弧燃烧指数(HAI)
|
PLC 1
|
|
UL 746 |
|
高电压电弧起痕速率 (HVTR)
|
PLC 2
|
|
UL 746 |
|
热丝引燃 (HWI)
|
PLC 2
|
|
UL 746 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级(1.47 mm)
|
HB
|
|
UL 94 |
| 光学性能 |
额定值
|
单位制
|
测试方法
|
|
折射率
|
1.586
|
|
ASTM D542 |
|
透射率(2540 μm)
|
88.0
|
%
|
ASTM D1003 |
|
雾度(2540 μm)
|
1.0
|
%
|
ASTM D1003 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
121
|
°C
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
干燥时间，最大
|
48
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 60
|
%
|
|
|
料筒后部温度
|
288 到 310
|
°C
|
|
|
料筒中部温度
|
299 到 321
|
°C
|
|
|
料筒前部温度
|
310 到 332
|
°C
|
|
|
射嘴温度
|
304 到 327
|
°C
|
|
|
加工（熔体）温度
|
310 到 332
|
°C
|
|
|
模具温度
|
82.2 到 116
|
°C
|
|
|
背压
|
0.345 到 0.689
|
MPa
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
0.025 到 0.076
|
mm
|
| 备注 |
| 1通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。 |
| 2UL 黄卡含有 UL 验证的易燃性和电气特性。 |
| 3类型 1, 50 mm/min |
| 41.3 mm/min |
| 5Type S |
6标准 B (120°C/h), 载荷2 (50N)  |