东莞市裕升高分子材料有限公司
500H物性表
物理性能额定值 (公制)额定值 (英制)测试方法
| 比重 | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| 线性成型收缩率,Flow | 0.012 - 0.016 cm/cm @Thickness 3.17 mm |
0.012 - 0.016 in/in @Thickness 0.125 in |
ASTM D955 |
| 线性成型收缩率，横向 | 0.012 - 0.016 cm/cm @Thickness 3.17 mm |
0.012 - 0.016 in/in @Thickness 0.125 in |
ASTM D955 |
| 熔体流动速率 | 25 g/10 min @Load 1.00 kg, Temperature 235 °C |
25 g/10 min @Load 2.20 lb, Temperature 455 °F |
Procedure A Condition Q; ASTM D1238 |
机械性能额定值 (公制)额定值 (英制)测试方法
| 肖氏硬度 (邵氏 A) | 77 | 77 | Instantaneous; ASTM D2240 |
| 抗张强度(屈服) | 34.5 MPa | 5000 psi | chs 20 in/min; ASTM D412 |
| 伸长率 (断裂) | 535 % | 535 % | ASTM D412 |
| 50% Modulus | 0.00300 GPa | 0.435 ksi | ASTM D412 |
| 100% 模量 | 0.00470 GPa | 0.682 ksi | ASTM D412 |
| 300％模量 | 0.00970 GPa | 1.41 ksi | ASTM D412 |
| 撕裂强度 | 87.5 kN/m | 499 pli | |
| 泰伯磨损，毫克/1000次 | 0.0551 | 0.0551 | H22 Wheel 1000 g load/1000 cycles; ASTM D3389 |
| 永久压缩 | 28 % @Temperature 100 °C |
28 % @Temperature 212 °F |
22 hours at 25% deflection; ASTM D395, Method B, |