RONFALIN? ASA 3323 U
Acrylonitrile Styrene Acrylate
Product Description:
ASA Compound with extra UV stabilization. (Former name: POLYMAN ASA WR/MI)
| General | |
|
Material Status
|
|
|
Literature1
|
|
|
Search for UL Yellow Card
|
|
|
Availability
|
|
|
Features
|
|
|
Processing Method
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
1.06
|
g/cm3
|
ISO 1183/A |
|
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg)
|
17
|
cm3/10min
|
ISO 1133 |
|
Molding Shrinkage
|
0.40 to 0.70
|
%
|
ISO 294-4 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Ball Indentation Hardness (H 358/30)
|
85.0
|
MPa
|
ISO 2039-1 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
2200
|
MPa
|
ISO 527-2/1A/1 |
|
Tensile Stress (Yield)
|
47.0
|
MPa
|
ISO 527-2/1A/50 |
|
Tensile Strain (Yield)
|
3.6
|
%
|
ISO 527-2/1A/50 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | ||
|
-30°C
|
3.0
|
kJ/m2
|
|
|
23°C
|
12
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | ||
|
-30°C
|
72
|
kJ/m2
|
|
|
23°C
|
No Break
|
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
|||
|
0.45 MPa, Unannealed
|
100
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, Unannealed
|
93.0
|
°C
|
ISO 75-2/Af |
|
Vicat Softening Temperature
|
|||
|
--
|
97.0
|
°C
|
ISO 306/B50 |
|
--
|
105
|
°C
|
ISO 306/A50 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E 15
|
ohms
|
IEC 60093 |
|
Volume Resistivity
|
1.0E 13
|
ohms·m
|
IEC 62631-3-1 |
|
Comparative Tracking Index (Solution A)
|
600
|
V
|
IEC 60112 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Burning Rate
|
|||
|
2.00 mm
|
100
|
mm/min
|
ISO 3795 |
|
2.00 mm
|
100
|
mm/min
|
FMVSS 302 |
|
Flammability Classification
|
IEC 60695-11-10, -20 | ||
|
1.5 mm
|
HB
|
||
|
3.0 mm
|
HB
|
| Additional Information | |||
|
1.) Not for use in food contact applications 2.) Not for use in medical or pharmaceutical applications
|
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
80
|
°C
|
|
|
Drying Time
|
2.0 to 4.0
|
hr
|
|
|
Suggested Max Regrind
|
30
|
%
|
|
|
Processing (Melt) Temp
|
240 to 270
|
°C
|
|
|
Mold Temperature
|
40 to 80
|
°C
|