This is a PC/ABS compound with colorable, good plating, surface and mechanical performance, a good candidate for Laser Direct Structuring applications
LNP? THERMOCOMP? NX11302 compound 物性表
基本信息
特性 | 可电镀 良好的着色性 优良外观 |
加工方法 | 注射成型 |
物理性能 额定值 单位制 测试方法
密度 | 1.22 | g/cm3 | ASTM D792 |
溶化体积流率(MVR)(260°C/5.0 kg) | 14.0 | cm3/10min | ISO 1133 |
收缩率 | ASTM D955 | ||
流动 : 24小时 | 0.60 | % | ASTM D955 |
横向流动 : 24小时 | 0.60 | % | ASTM D955 |
吸水率 | ASTM D570 | ||
24 hr | 0.010 | % | ASTM D570 |
24 hr, 50% RH | 0.010 | % | ASTM D570 |
机械性能 额定值 单位制 测试方法
拉伸模量1 | 2350 | MPa | ASTM D638 |
抗张强度2 | ASTM D638 | ||
屈服 | 47.0 | MPa | ASTM D638 |
断裂 | 46.0 | MPa | ASTM D638 |
伸长率3 | ASTM D638 | ||
屈服 | 4.6 | % | ASTM D638 |
断裂 | 75 | % | ASTM D638 |
弯曲模量4(50.0 mm 跨距) | 2230 | MPa | ASTM D790 |
弯曲强度5 | ASTM D790 | ||
屈服, 50.0 mm 跨距 | 79.0 | MPa | ASTM D790 |
断裂, 50.0 mm 跨距 | 78.0 | MPa | ASTM D790 |
冲击性能 额定值 单位制 测试方法
悬壁梁缺口冲击强度(23°C) | 550 | J/m | ASTM D256 |
热性能 额定值 单位制 测试方法
载荷下热变形温度(1.8 MPa, 未退火, 3.20 mm) | 106 | °C | ASTM D648 |
线形热膨胀系数 | ASTM E831 | ||
流动 : -40 到 40°C | 7.1E-5 | cm/cm/°C | ASTM E831 |
横向 : -40 到 40°C | 7.6E-5 | cm/cm/°C | ASTM E831 |
电气性能 额定值测试方法
相对电容率(1.00 GHz) | 2.94 | IEC 60250 | |
耗散因数(1.00 GHz) | 5.7E-3 | IEC 60250 |