东莞市裕升高分子材料有限公司
Luran? S KR2858G3
Acrylonitrile Styrene Acrylate
Product Description:
Luran? S KR2858G3 is a 15% glass fiber reinforced grade offering enhanced heat resistance and superior rigidity. FEATURES APPLICATIONS
| General | |
|
Material Status
|
|
|
Literature1
|
|
|
Search for UL Yellow Card
|
|
|
Availability
|
|
|
Filler / Reinforcement
|
|
|
Features
|
|
|
Uses
|
|
|
Forms
|
|
|
Processing Method
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
1.18
|
g/cm3
|
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg)
|
5.0
|
cm3/10min
|
ISO 1133 |
|
Molding Shrinkage2
|
0.40
|
%
|
ISO 294-4 |
|
Water Absorption
|
ISO 62 | ||
|
Saturation, 23°C
|
1.4
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
0.30
|
%
|
|
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Ball Indentation Hardness
|
170
|
MPa
|
ISO 2039-1 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
6600
|
MPa
|
ISO 527-2 |
|
Tensile Stress (Break, 23°C)
|
110
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Break, 23°C)
|
2.5
|
%
|
ISO 527-2 |
|
Flexural Stress (23°C)
|
140
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | ||
|
-30°C
|
5.0
|
kJ/m2
|
|
|
23°C
|
7.0
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179 | ||
|
-30°C
|
17
|
kJ/m2
|
|
|
23°C
|
28
|
kJ/m2
|
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature3
|
|||
|
0.45 MPa, Annealed
|
115
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Annealed
|
110
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
|||
|
--
|
115
|
°C
|
ISO 306/B50 |
|
--
|
120
|
°C
|
ISO 306/A50 |
|
CLTE - Flow
|
3.0E-5
|
cm/cm/°C
|
ISO 11359-2 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
80
|
°C
|
|
|
Drying Time
|
2.0 to 4.0
|
hr
|
|
|
Processing (Melt) Temp
|
240 to 280
|
°C
|
|
|
Mold Temperature
|
40 to 95
|
°C
|
|
|
Injection Velocity
|
12
|
m/min
|
| Notes |
| 1These links provide you with access to supplier literature. We work hard to keep them up to date; however you may find the most current literature from the supplier. |