VALOX? Resin VX4915R - Europe
Polybutylene Terephthalate ASA
Product Description:
15% Glass reinforced nucleated PBT/ASA improved release, with excellent mechanical properties high dimensional stability, and low density.
| General | |
|
Material Status
|
|
|
Search for UL Yellow Card
|
|
|
Availability
|
|
|
Uses
|
|
|
RoHS Compliance
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
1.31
|
g/cm3
|
ASTM D792,ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (265°C/5.0 kg)
|
33
|
g/10 min
|
ASTM D1238 |
|
Melt Volume-Flow Rate (MVR)
|
ISO 1133 | ||
|
250°C/5.0 kg
|
20
|
cm3/10min
|
|
|
265°C/5.0 kg
|
30
|
cm3/10min
|
|
|
Molding Shrinkage1
|
Internal Method | ||
|
Across Flow
|
0.30 to 0.70
|
%
|
|
|
Flow
|
0.20 to 0.60
|
%
|
|
|
Water Absorption
|
ISO 62 | ||
|
Saturation, 23°C
|
0.80
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
0.30
|
%
|
|
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness (R-Scale)
|
120
|
ISO 2039-2 | |
|
Ball Indentation Hardness (H 358/30)
|
100
|
MPa
|
ISO 2039-1 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
|||
|
--2
|
5600
|
MPa
|
ASTM D638 |
|
--
|
5700
|
MPa
|
ISO 527-2/1 |
|
Tensile Strength
|
|||
|
Yield3
|
85.0
|
MPa
|
ASTM D638 |
|
Yield
|
80.0
|
MPa
|
ISO 527-2/5 |
|
Break3
|
85.0
|
MPa
|
ASTM D638 |
|
Break
|
80.0
|
MPa
|
ISO 527-2/5 |
|
Tensile Elongation
|
|||
|
Yield3
|
3.0
|
%
|
ASTM D638 |
|
Yield
|
4.0
|
%
|
ISO 527-2/5 |
|
Break3
|
3.0
|
%
|
ASTM D638 |
|
Break
|
4.0
|
%
|
ISO 527-2/5 |
|
Flexural Modulus
|
|||
|
50.0 mm Span4
|
4200
|
MPa
|
ASTM D790 |
|
--5
|
4600
|
MPa
|
ISO 178 |
|
Flexural Stress
|
|||
|
--5,6
|
130
|
MPa
|
ISO 178 |
|
Yield, 50.0 mm Span4
|
125
|
MPa
|
ASTM D790 |
|
Break, 50.0 mm Span4
|
125
|
MPa
|
ASTM D790 |
|
Flexural Strain - at Break7
|
4.0
|
%
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/2C | ||
|
-30°C
|
6.0
|
kJ/m2
|
|
|
23°C
|
6.0
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/2U | ||
|
-30°C
|
30
|
kJ/m2
|
|
|
23°C
|
45
|
kJ/m2
|
|
|
Notched Izod Impact
|
|||
|
-30°C
|
50
|
J/m
|
ASTM D256 |
|
0°C
|
60
|
J/m
|
ASTM D256 |
|
23°C
|
65
|
J/m
|
ASTM D256 |
|
-30°C8
|
5.0
|
kJ/m2
|
ISO 180/1A |
|
0°C8
|
6.0
|
kJ/m2
|
ISO 180/1A |
|
23°C8
|
6.0
|
kJ/m2
|
ISO 180/1A |
|
Unnotched Izod Impact
|
|||
|
-30°C
|
490
|
J/m
|
ASTM D4812 |
|
23°C
|
520
|
J/m
|
ASTM D4812 |
|
-30°C8
|
25
|
kJ/m2
|
ISO 180/1U |
|
23°C8
|
35
|
kJ/m2
|
ISO 180/1U |