GELOY? Resin XP7550 - Asia
Polycarbonate ASA
Product Description:
PC/ASA. Excellent weatherability.
| General | |
|
Material Status
|
|
|
Search for UL Yellow Card
|
|
|
Availability
|
|
|
Features
|
|
|
Uses
|
|
|
Processing Method
|
|
|
Also Available In
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
1.11
|
g/cm3
|
ASTM D792,ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (220°C/10.0 kg)
|
14
|
g/10 min
|
ASTM D1238 |
|
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg)
|
26
|
cm3/10min
|
ISO 1133 |
|
Molding Shrinkage
|
Internal Method | ||
|
Flow1
|
0.50 to 0.70
|
%
|
|
|
Across Flow : 3.20 mm
|
0.50 to 0.70
|
%
|
|
|
Flow : 3.20 mm
|
0.40 to 0.60
|
%
|
|
|
Water Absorption
|
ISO 62 | ||
|
Saturation, 23°C
|
0.80
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
0.30
|
%
|
|
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness (R-Scale)
|
109
|
ASTM D785 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
|||
|
--2
|
2550
|
MPa
|
ASTM D638 |
|
--
|
2550
|
MPa
|
ISO 527-2/1 |
|
Tensile Strength
|
|||
|
Yield3
|
56.0
|
MPa
|
ASTM D638 |
|
Yield
|
55.0
|
MPa
|
ISO 527-2/50 |
|
Break3
|
44.0
|
MPa
|
ASTM D638 |
|
Break
|
44.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Elongation
|
|||
|
Yield3
|
4.0
|
%
|
ASTM D638 |
|
Yield
|
3.8
|
%
|
ISO 527-2/50 |
|
Break3
|
40
|
%
|
ASTM D638 |
|
Break
|
37
|
%
|
ISO 527-2/50 |
|
Flexural Modulus
|
|||
|
50.0 mm Span4
|
2480
|
MPa
|
ASTM D790 |
|
--5
|
2400
|
MPa
|
ISO 178 |
|
Flexural Stress
|
|||
|
--5,6
|
74.0
|
MPa
|
ISO 178 |
|
Yield, 50.0 mm Span4
|
82.0
|
MPa
|
ASTM D790 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength7 (23°C)
|
40
|
kJ/m2
|
ISO 179/1eA |
|
Notched Izod Impact
|
|||
|
-30°C
|
53
|
J/m
|
ASTM D256 |
|
23°C
|
380
|
J/m
|
ASTM D256 |
|
-30°C8
|
9.0
|
kJ/m2
|
ISO 180/1A |
|
23°C8
|
35
|
kJ/m2
|
ISO 180/1A |
|
Instrumented Dart Impact
|
ASTM D3763 | ||
|
-30°C, Total Energy
|
10.0
|
J
|
|
|
23°C, Total Energy
|
36.0
|
J
|
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
|||
|
0.45 MPa, Unannealed, 3.20 mm
|
104
|
°C
|
ASTM D648 |
|
0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span8
|
103
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, Unannealed, 3.20 mm
|
89.0
|
°C
|
ASTM D648 |
|
1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8
|
89.0
|
°C
|
ISO 75-2/Af |
|
Vicat Softening Temperature
|
|||
|
--
|
105
|
°C
|
ASTM D15259,ISO 306/B509 |
|
--
|
106
|
°C
|
ISO 306/B120 |
|
Ball Pressure Test (83 to 87°C)
|
Pass
|
IEC 60695-10-2 | |
|
CLTE
|
|||
|
Flow : -40 to 40°C
|
7.2E-5
|
cm/cm/°C
|
ASTM E831,ISO 11359-2 |
|
Transverse : -40 to 40°C
|
7.9E-5
|
cm/cm/°C
|
ASTM E831 |
|
Transverse : -40°C
|
7.8E-5
|
cm/cm/°C
|
ISO 11359-2 |
| Optical |
Nominal Value
|
Test Method
|
|
|
Gloss (60°, Untextured)
|
94
|
ASTM D523 |