Asaflex? 825苯乙烯-丁二烯-苯乙烯嵌段共聚物AKelastomers产品说明：

Injection- and blow-molding grade. For transparent products with superior impact strength. Blended with GPPS (general-purpose polystyrene) or SC*, for films with good thermal stability. Capability for profile-extrusion products. It is supplied in pellet form. Cosmetics caps, stationery goods, other consumer goods. Blended with GPPS for PSP* laminate films and IC magazine rails, and with SC* for shrink films. * Styrenic copolymer from PS Japan Corp. similar to Asaflex? 825 in refraction index, resulting in blends that provide sheet transparency significantly higher than attainable with any GPPS.

Asaflex? 825 物性表

基本信息

特性	共聚物 抗撞击性，高 清晰度，高 热稳定性，良好
用途	Cosmetic Packaging Water Sports Equipment 薄膜 层压板 文具 消费品应用领域 型材
外观	清晰/透明
形式	粒子
加工方法	吹塑成型 型材挤出成型 注射成型

物理性能额定值单位制测试方法

密度	1.02	g/cm3	ISO 1183
熔流率（熔体流动速率）(200°C/5.0 kg)	6.0	g/10 min	ISO 1133
收缩率	0.20 到 0.80	%
吸水率(23°C, 24 hr)	0.10	%	ISO 62

硬度额定值单位制测试方法

洛氏硬度(R 计秤)	55		ISO 2039-2
肖氏硬度(邵氏 D)	71		ISO 868

机械性能额定值单位制测试方法

拉伸应力(屈服)	27.0	MPa	ISO 527-2/5
拉伸应变(断裂)	200	%	ISO 527-2/5
弯曲模量	1200	MPa	ISO 178
弯曲应力	37.0	MPa	ISO 178

冲击性能额定值单位制测试方法

简支梁缺口冲击强度(完全断裂)	2.0	kJ/m2	ISO 179
简支梁无缺口冲击强度(完全断裂)	100	kJ/m2	ISO 179

热性能额定值单位制测试方法

热变形温度(1.8 MPa, 未退火)	57.0	°C	ISO 75-2/A
维卡软化温度	82.0	°C	ISO 306/A50

光学性能额定值单位制测试方法

透射率(2000 μm)	90.0	%	ISO 3537
雾度(2000 μm)	0.50	%	ISO 3537