东莞市裕升高分子材料有限公司
GELOY? Resin XTPMFR10 - Asia
Polycarbonate ASA
Product Description:
PC/ASA, chlorine and bromine free.
| General | |
|
Material Status
|
|
|
UL Yellow Card1
|
|
|
Search for UL Yellow Card
|
|
|
Availability
|
|
|
Features
|
|
|
Uses
|
|
|
Processing Method
|
|
|
Also Available In
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
1.18
|
g/cm3
|
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (260°C/2.16 kg)
|
30
|
cm3/10min
|
ISO 1133 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
|||
|
--2
|
2680
|
MPa
|
ASTM D638 |
|
--
|
2680
|
MPa
|
ISO 527-2/1 |
|
Tensile Strength
|
|||
|
Yield3
|
65.0
|
MPa
|
ASTM D638 |
|
Yield4
|
60.0
|
MPa
|
ASTM D638 |
|
Yield
|
61.0
|
MPa
|
ISO 527-2/5 |
|
Yield
|
66.0
|
MPa
|
ISO 527-2/50 |
|
Break4
|
49.0
|
MPa
|
ASTM D638 |
|
Break3
|
47.0
|
MPa
|
ASTM D638 |
|
Break
|
46.0
|
MPa
|
ISO 527-2/5 |
|
Break
|
47.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Elongation
|
|||
|
Yield4
|
4.0
|
%
|
ASTM D638 |
|
Yield3
|
4.0
|
%
|
ASTM D638 |
|
Yield
|
4.0
|
%
|
ISO 527-2/5,ISO 527-2/50 |
|
Break4
|
58
|
%
|
ASTM D638 |
|
Break3
|
31
|
%
|
ASTM D638 |
|
Break
|
50
|
%
|
ISO 527-2/5 |
|
Break
|
21
|
%
|
ISO 527-2/50 |
|
Flexural Modulus5
|
2720
|
MPa
|
ISO 178 |
|
Flexural Stress5,6
|
97.0
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength7 (23°C)
|
13
|
kJ/m2
|
ISO 179/1eA |
|
Notched Izod Impact
|
|||
|
-30°C
|
90
|
J/m
|
ASTM D256 |
|
23°C
|
330
|
J/m
|
ASTM D256 |
|
0°C8
|
12
|
kJ/m2
|
ISO 180/1A |
|
23°C8
|
13
|
kJ/m2
|
ISO 180/1A |
|
Multi-Axial Instrumented Impact Energy
|
85.0
|
J
|
ISO 6603-2 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature8
|
|||
|
0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span
|
90.0
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span
|
81.0
|
°C
|
ISO 75-2/Af |
|
Vicat Softening Temperature
|
|||
|
--
|
98.0
|
°C
|
ISO 306/B120 |
|
--
|
96.0
|
°C
|
ISO 306/B50 |
|
CLTE
|
ISO 11359-2 | ||
|
Flow : -40 to 40°C
|
6.3E-5
|
cm/cm/°C
|
|
|
Transverse : -40°C
|
6.3E-5
|
cm/cm/°C
|
| Flammability |
Nominal Value
|
Test Method
|
|
|
Flame Rating (1.0 mm, Testing by SABIC)
|
V-0
|
UL 94 |
| Fill Analysis |
Nominal Value
|
Unit
|
Test Method
|
|
Melt Viscosity (260°C, 1500 sec^-1)
|
105
|
Pa·s
|
ISO 11443 |