东莞市裕升高分子材料有限公司
Bayblend? W85 XF
Polycarbonate ASA
Product Description:
PC ASA-Blend; Vicat/B 120 temperature = 134°C; improved weather resistance; excellent low temperature ductility; excellent low temperature ductility; good heat resistance
| General | |
|
Material Status
|
|
|
Literature1
|
|
|
UL Yellow Card2
|
|
|
Search for UL Yellow Card
|
|
|
Availability
|
|
|
Features
|
|
|
RoHS Compliance
|
|
|
Processing Method
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density (23°C)
|
1.16
|
g/cm3
|
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg)
|
27
|
cm3/10min
|
ISO 1133 |
|
Molding Shrinkage3
|
ISO 2577 | ||
|
Across Flow : 260°C, 3.00 mm
|
0.55 to 0.75
|
%
|
|
|
Flow : 260°C, 3.00 mm
|
0.55 to 0.75
|
%
|
|
|
Water Absorption
|
ISO 62 | ||
|
Saturation, 23°C
|
0.50
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
0.20
|
%
|
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
2450
|
MPa
|
ISO 527-2/1 |
|
Tensile Stress
|
ISO 527-2/50 | ||
|
Yield, 23°C
|
63.0
|
MPa
|
|
|
Break, 23°C
|
62.0
|
MPa
|
|
|
Tensile Strain
|
ISO 527-2/50 | ||
|
Yield, 23°C
|
5.0
|
%
|
|
|
Break, 23°C
|
50
|
%
|
|
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact Strength
|
ISO 180/A | ||
|
-20°C
|
15
|
kJ/m2
|
|
|
23°C
|
45
|
kJ/m2
|
|
|
Unnotched Izod Impact Strength
|
ISO 180 | ||
|
-30°C
|
No Break
|
||
|
23°C
|
No Break
|
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
|||
|
0.45 MPa, Unannealed
|
127
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
109
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
|||
|
--
|
132
|
°C
|
ISO 306/B120 |
|
--
|
130
|
°C
|
ISO 306/B50 |
|
CLTE
|
ISO 11359-2 | ||
|
Flow : 23 to 55°C
|
7.0E-5
|
cm/cm/°C
|
|
|
Transverse : 23 to 55°C
|
7.0E-5
|
cm/cm/°C
|
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E 16
|
ohms
|
IEC 60093 |
|
Volume Resistivity (23°C)
|
1.0E 16
|
ohms·cm
|
IEC 60093 |
|
Electric Strength (23°C, 1.00 mm)
|
35
|
kV/mm
|
IEC 60243-1 |
|
Relative Permittivity
|
IEC 60250 | ||
|
23°C, 100 Hz
|
3.10
|
||
|
23°C, 1 MHz
|
2.80
|
||
|
Dissipation Factor
|
IEC 60250 | ||
|
23°C, 100 Hz
|
2.5E-3
|
||
|
23°C, 1 MHz
|
0.011
|
||
|
Comparative Tracking Index (Solution A)
|
225
|
V
|
IEC 60112 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating (0.9 mm)
|
HB
|
UL 94 | |
|
Oxygen Index4
|
25
|
%
|
ISO 4589-2 |
| Fill Analysis |
Nominal Value
|
Unit
|
Test Method
|
|
Melt Viscosity5 (260°C)
|
225
|
Pa·s
|
ISO 11443-A |
| Additional Information |
Nominal Value
|
Unit
|
Test Method
|
|
ISO Shortname
|
PC ASA
|