VALOX? Resin VX4910 - Europe
Polybutylene Terephthalate ASA
Product Description:
10% Glass reinforced nucleated PBT/ASA with excellent mechanical properties high dimensional stability, and low density.
| General | |
|
Material Status
|
|
|
Search for UL Yellow Card
|
|
|
Availability
|
|
|
Uses
|
|
|
RoHS Compliance
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
1.30
|
g/cm3
|
ASTM D792,ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
ASTM D1238 | ||
|
200°C/3.8 kg
|
20
|
g/10 min
|
|
|
265°C/5.0 kg
|
40
|
g/10 min
|
|
|
Melt Volume-Flow Rate (MVR)
|
ISO 1133 | ||
|
250°C/5.0 kg
|
25
|
cm3/10min
|
|
|
265°C/5.0 kg
|
35
|
cm3/10min
|
|
|
Molding Shrinkage - Flow (3.20 mm)
|
0.60 to 0.80
|
%
|
Internal Method |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness (R-Scale)
|
120
|
ISO 2039-2 | |
|
Ball Indentation Hardness (H 358/30)
|
100
|
MPa
|
ISO 2039-1 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
|||
|
--1
|
4600
|
MPa
|
ASTM D638 |
|
--
|
4600
|
MPa
|
ISO 527-2/1 |
|
Tensile Strength
|
|||
|
Yield2
|
80.0
|
MPa
|
ASTM D638 |
|
Yield
|
80.0
|
MPa
|
ISO 527-2/5 |
|
Break2
|
80.0
|
MPa
|
ASTM D638 |
|
Break
|
80.0
|
MPa
|
ISO 527-2/5 |
|
Tensile Elongation
|
|||
|
Yield2
|
3.0
|
%
|
ASTM D638 |
|
Yield
|
3.0
|
%
|
ISO 527-2/5 |
|
Break2
|
3.0
|
%
|
ASTM D638 |
|
Break
|
3.0
|
%
|
ISO 527-2/5 |
|
Flexural Modulus
|
|||
|
50.0 mm Span3
|
3400
|
MPa
|
ASTM D790 |
|
--4
|
3800
|
MPa
|
ISO 178 |
|
Flexural Stress
|
|||
|
--4,5
|
120
|
MPa
|
ISO 178 |
|
--4,6
|
115
|
MPa
|
ISO 178 |
|
Yield, 50.0 mm Span3
|
115
|
MPa
|
ASTM D790 |
|
Break, 50.0 mm Span3
|
115
|
MPa
|
ASTM D790 |
|
Flexural Strain - at Break7
|
4.0
|
%
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/2C | ||
|
-30°C
|
5.0
|
kJ/m2
|
|
|
23°C
|
6.0
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/2U | ||
|
-30°C
|
20
|
kJ/m2
|
|
|
23°C
|
45
|
kJ/m2
|
|
|
Notched Izod Impact
|
|||
|
-30°C
|
45
|
J/m
|
ASTM D256 |
|
0°C
|
50
|
J/m
|
ASTM D256 |
|
23°C
|
55
|
J/m
|
ASTM D256 |
|
-30°C8
|
5.0
|
kJ/m2
|
ISO 180/1A |
|
0°C8
|
5.0
|
kJ/m2
|
ISO 180/1A |
|
23°C8
|
5.0
|
kJ/m2
|
ISO 180/1A |
|
Unnotched Izod Impact
|
|||
|
-30°C
|
340
|
J/m
|
ASTM D4812 |
|
23°C
|
440
|
J/m
|
ASTM D4812 |
|
-30°C8
|
25
|
kJ/m2
|
ISO 180/1U |
|
23°C8
|
30
|
kJ/m2
|
ISO 180/1U |
|
Instrumented Dart Impact (23°C, Total Energy)
|
45.0
|
J
|
ASTM D3763 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
|||
|
0.45 MPa, Unannealed, 3.20 mm
|
205
|
°C
|
ASTM D648 |
|
0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span8
|
205
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, Unannealed, 3.20 mm
|
130
|
°C
|
ASTM D648 |
|
1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8
|
130
|
°C
|
ISO 75-2/Af |
|
Vicat Softening Temperature
|
|||
|
--
|
218
|
°C
|
ASTM D15259,ISO 306/A509 |
|
--
|
150
|
°C
|
ASTM D152510,ISO 306/B5010 |
|
--
|
155
|
°C
|
ISO 306/B120 |
|
Ball Pressure Test (123 to 127°C)
|
Pass
|
IEC 60695-10-2 | |
|
CLTE
|
ISO 11359-2 | ||
|
Flow : -40 to 40°C
|
4.1E-5
|
cm/cm/°C
|
|
|
Flow : 23 to 60°C
|
5.0E-5
|
cm/cm/°C
|
|
|
Flow : 23 to 150°C
|
3.6E-5
|
cm/cm/°C
|
|
|
Transverse : -40°C
|
8.1E-5
|
cm/cm/°C
|
|
|
Transverse : 23 to 60°C
|
1.2E-4
|
cm/cm/°C
|
|
|
Transverse : 23 to 150°C
|
2.0E-4
|
cm/cm/°C
|
| Electrical |
Nominal Value
|
Test Method
|
|
|
Dielectric Constant (1 MHz)
|
3.40
|
ASTM D150,IEC 60250 | |
|
Dissipation Factor (1 MHz)
|
0.020
|
ASTM D150,IEC 60250 |
| Fill Analysis |
Nominal Value
|
Unit
|
Test Method
|
|
Melt Viscosity (260°C, 1500 sec^-1)
|
160
|
Pa·s
|
ISO 11443 |
| Additional Information |
Nominal Value
|
Unit
|
Test Method
|
|
Filler Content
|
10
|
%
|
ASTM D229 |