GELOY? Resin CR8510 - Asia
Acrylonitrile Styrene Acrylate
Product Description:
ASA, excellent weatherability, injection molding.
| General | |
|
Material Status
|
|
|
UL Yellow Card1
|
|
|
Search for UL Yellow Card
|
|
|
Availability
|
|
|
Features
|
|
|
Uses
|
|
|
Processing Method
|
|
|
Also Available In
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
|||
|
--
|
1.08
|
g/cm3
|
ASTM D792 |
|
--
|
1.07
|
g/cm3
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
ASTM D1238 | ||
|
220°C/10.0 kg
|
6.3
|
g/10 min
|
|
|
260°C/5.0 kg
|
11
|
g/10 min
|
|
|
280°C/3.8 kg
|
7.8
|
g/10 min
|
|
|
Melt Volume-Flow Rate (MVR)
|
ISO 1133 | ||
|
220°C/10.0 kg
|
6.0
|
cm3/10min
|
|
|
260°C/5.0 kg
|
10
|
cm3/10min
|
|
|
Molding Shrinkage - Flow (3.20 mm)
|
0.50 to 0.80
|
%
|
Internal Method |
|
Water Absorption
|
ISO 62 | ||
|
Saturation, 23°C
|
0.50
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
0.20
|
%
|
|
|
Outdoor Suitability
|
f1
|
UL 746C | |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness (R-Scale)
|
93
|
ASTM D785 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
|||
|
--2
|
1970
|
MPa
|
ASTM D638 |
|
--3
|
2070
|
MPa
|
ASTM D638 |
|
--
|
2040
|
MPa
|
ISO 527-2/1 |
|
Tensile Strength
|
|||
|
Yield4
|
40.0
|
MPa
|
ASTM D638 |
|
Yield
|
43.0
|
MPa
|
ISO 527-2/50 |
|
Break4
|
33.0
|
MPa
|
ASTM D638 |
|
Break
|
19.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Elongation
|
|||
|
Yield4
|
3.6
|
%
|
ASTM D638 |
|
Yield
|
3.3
|
%
|
ISO 527-2/50 |
|
Break4
|
60
|
%
|
ASTM D638 |
|
Break
|
35
|
%
|
ISO 527-2/50 |
|
Flexural Modulus
|
|||
|
50.0 mm Span5
|
2170
|
MPa
|
ASTM D790 |
|
--6
|
2060
|
MPa
|
ISO 178 |
|
Flexural Stress
|
|||
|
--6,7
|
64.0
|
MPa
|
ISO 178 |
|
Yield, 50.0 mm Span5
|
68.0
|
MPa
|
ASTM D790 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength8 (23°C)
|
14
|
kJ/m2
|
ISO 179/1eA |
|
Notched Izod Impact
|
|||
|
-30°C
|
60
|
J/m
|
ASTM D256 |
|
23°C
|
400
|
J/m
|
ASTM D256 |
|
-30°C9
|
6.0
|
kJ/m2
|
ISO 180/1A |
|
23°C9
|
15
|
kJ/m2
|
ISO 180/1A |
|
Instrumented Dart Impact
|
ASTM D3763 | ||
|
-30°C, Total Energy
|
4.00
|
J
|
|
|
23°C, Total Energy
|
30.0
|
J
|
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
|||
|
0.45 MPa, Unannealed, 3.20 mm
|
103
|
°C
|
ASTM D648 |
|
0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span9
|
103
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, Unannealed, 3.20 mm
|
90.0
|
°C
|
ASTM D648 |
|
1.8 MPa, Unannealed, 4.00 mm, 100 mm Span10
|
88.0
|
°C
|
ISO 75-2/Ae |
|
1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9
|
89.0
|
°C
|
ISO 75-2/Af |
|
Vicat Softening Temperature
|
|||
|
--
|
98.0
|
°C
|
ASTM D152511 |
|
--
|
105
|
°C
|
ISO 306/B120 |
|
--
|
102
|
°C
|
ISO 306/B50 |
|
Ball Pressure Test12 (98°C)
|
Pass
|
IEC 60695-10-2 | |
|
CLTE
|
|||
|
Flow : -40 to 40°C
|
8.4E-5
|
cm/cm/°C
|
ASTM E831,ISO 11359-2 |
|
Transverse : -40 to 40°C
|
9.5E-5
|
cm/cm/°C
|
ASTM E831 |
|
Transverse : -40°C
|
9.5E-5
|
cm/cm/°C
|
ISO 11359-2 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Dissipation Factor
|
ASTM D150 | ||
|
100 kHz
|
0.018
|
||
|
1 MHz
|
0.026
|
||
|
Comparative Tracking Index
|
600
|
V
|
IEC 60112 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating (1.5 mm)
|
HB
|
UL 94 |
| Optical |
Nominal Value
|
Test Method
|
|
|
Gloss (60°, Untextured)
|
94
|
ASTM D523 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
85 to 90
|
°C
|
|
|
Drying Time
|
4.0
|
hr
|
|
|
Suggested Max Moisture
|
0.040
|
%
|
|
|
Suggested Shot Size
|
40 to 80
|
%
|
|
|
Rear Temperature
|
215 to 250
|
°C
|
|
|
Middle Temperature
|
220 to 255
|
°C
|
|
|
Front Temperature
|
230 to 260
|
°C
|
|
|
Nozzle Temperature
|
220 to 255
|
°C
|
|
|
Processing (Melt) Temp
|
240 to 270
|
°C
|
|
|
Mold Temperature
|
60 to 85
|
°C
|
|
|
Back Pressure
|
0.300 to 1.00
|
MPa
|
|
|
Screw Speed
|
30 to 80
|
rpm
|
|
|
Vent Depth
|
0.038 to 0.076
|
mm
|
|
| Injection Notes | |||
|
Injection Molding Parameters
|
|||