Luran? S 747R
Acrylonitrile Styrene Acrylate
Product Description:
Luran? S 747R is a high flow, low gloss extrusion grade with enhanced strength properities. The enhanced flow properties make the product suitable for co-extruded applications FEATURES APPLICATIONS
| General | |
|
Material Status
|
|
|
Literature1
|
|
|
Search for UL Yellow Card
|
|
|
Availability
|
|
|
Features
|
|
|
Uses
|
|
|
Forms
|
|
|
Processing Method
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
1.09
|
g/cm3
|
ASTM D792 |
|
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg)
|
7.0
|
cm3/10min
|
ASTM D1238 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness (R-Scale)
|
110
|
ASTM D785 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength (Yield, 23°C)
|
53.1
|
MPa
|
ASTM D638 |
|
Tensile Elongation (Yield, 23°C)
|
3.0
|
%
|
ASTM D638 |
|
Flexural Modulus
|
2450
|
MPa
|
ASTM D790 |
|
Flexural Strength (23°C)
|
75.2
|
MPa
|
ASTM D790 |
| Films |
Nominal Value
|
Unit
|
Test Method
|
|
Elastic Modulus - MD
|
234
|
MPa
|
ASTM D882 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact
|
ASTM D256 | ||
|
-40°C
|
16
|
J/m
|
|
|
23°C
|
110
|
J/m
|
|
|
Instrumented Dart Impact (Total Energy)
|
9.04
|
J
|
ASTM D3763 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
|||
|
1.8 MPa, Annealed
|
87.8
|
°C
|
ASTM D648 |
|
1.8 MPa, Annealed2
|
93.3
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
100
|
°C
|
ISO 306/A50 |
| Injection |
Nominal Value
|
Unit
|
|
|
Mold Temperature
|
40 to 80
|
°C
|
|
| Extrusion |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
80
|
°C
|
|
|
Melt Temperature
|
240 to 280
|
°C
|
| Notes |
| 1These links provide you with access to supplier literature. We work hard to keep them up to date; however you may find the most current literature from the supplier.Luran? S 767KE
Acrylonitrile Styrene Acrylate
Product Description:
Luran? S 767KE is particular suitable for co-extrusion with PVC at low temperature. Hereby, it provides a glossy surface finish. FEATURES APPLICATIONS
GeneralMaterial Status Literature1 Search for UL Yellow Card Availability Features Uses Forms Processing Method
PhysicalNominal ValueUnitTest MethodDensity1.07g/cm3ISO 1183Apparent (Bulk) Density20.59g/cm3Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) 17cm3/10minISO 1133Molding Shrinkage0.50 to 0.90%ISO 294-4Water Absorption ISO 62Saturation, 23°C 1.7%Equilibrium, 23°C, 50% RH 0.35%HardnessNominal ValueUnitTest MethodBall Indentation Hardness80.0MPaISO 2039-1
MechanicalNominal ValueUnitTest MethodTensile Modulus2300MPaISO 527-2Tensile Stress (Yield, 23°C) 50.0MPaISO 527-2Tensile Strain (Yield, 23°C) 3.3%ISO 527-2Nominal Tensile Strain at Break (23°C) 8.0%ISO 527-2Tensile Creep Modulus (1000 hr) 1400MPaISO 899-1Flexural Stress (23°C) 70.0MPaISO 178ImpactNominal ValueUnitTest MethodCharpy Notched Impact Strength ISO 179/1eA-30°C 4.0kJ/m223°C 10kJ/m2
ThermalNominal ValueUnitTest MethodHeat Deflection Temperature3 0.45 MPa, Annealed 101°CISO 75-2/B1.8 MPa, Annealed 97.0°CISO 75-2/AVicat Softening Temperature -- 98.0°CISO 306/B50-- 105°CISO 306/A50CLTE - Flow8.0E-5 to 1.1E-4cm/cm/°CISO 11359-2Thermal Conductivity0.17W/m/KDIN 52612
ElectricalNominal ValueUnitTest MethodSurface Resistivity1.0E 13ohmsIEC 60093Volume Resistivity1.0E 14ohms·cmIEC 60093Dielectric Constant 100 Hz 3.70IEC 602501 MHz 3.40IEC 60250Dissipation Factor IEC 60250100 Hz 0.0111 MHz 0.024
InjectionNominal ValueUnitDrying Temperature80°CDrying Time2.0 to 4.0hrProcessing (Melt) Temp200 to 250°C
Notes1These links provide you with access to supplier literature. We work hard to keep them up to date; however you may find the most current literature from the supplier.
|