Bayblend? W90 XG
Polycarbonate ASA
Product Description:
PC ASA-Blend; Vicat/B 120 temperature = 115°C; UV-stabilized; very good surface finish
| General | |
|
Material Status
|
|
|
Literature1
|
|
|
UL Yellow Card2
|
|
|
Search for UL Yellow Card
|
|
|
Availability
|
|
|
Additive
|
|
|
Features
|
|
|
RoHS Compliance
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density (23°C)
|
1.14
|
g/cm3
|
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg)
|
34
|
cm3/10min
|
ISO 1133 |
|
Molding Shrinkage3
|
ISO 294-4 | ||
|
Across Flow : 2.00 mm
|
0.50 to 0.70
|
%
|
|
|
Flow : 2.00 mm
|
0.50 to 0.70
|
%
|
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
2830
|
MPa
|
ISO 527-2/1 |
|
Tensile Stress
|
ISO 527-2/50 | ||
|
Yield, 23°C
|
65.0
|
MPa
|
|
|
Break, 23°C
|
50.0
|
MPa
|
|
|
Tensile Strain
|
ISO 527-2/50 | ||
|
Yield, 23°C
|
4.0
|
%
|
|
|
Break, 23°C
|
50
|
%
|
|
|
Flexural Modulus4 (23°C)
|
MPa
|
ISO 178 | |
|
Flexural Stress4 (3.5% Strain, 23°C)
|
85.0
|
MPa
|
ISO 178 |
|
Flexural Strain at Flexural Strength5 (23°C)
|
5.0
|
%
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact Strength
|
ISO 180/A | ||
|
-30°C
|
7.0
|
kJ/m2
|
|
|
23°C
|
14
|
kJ/m2
|
|
|
Multi-Axial Instrumented Impact Energy
|
ISO 6603-2 | ||
|
-30°C
|
20.0
|
J
|
|
|
23°C
|
45.0
|
J
|
|
|
Multi-Axial Instrumented Impact Peak Force
|
ISO 6603-2 | ||
|
-30°C
|
4250
|
N
|
|
|
23°C
|
4800
|
N
|
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
|||
|
0.45 MPa, Unannealed
|
112
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
93.0
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
|||
|
--
|
115
|
°C
|
ISO 306/B120 |
|
--
|
113
|
°C
|
ISO 306/B50 |
|
CLTE
|
ISO 11359-2 | ||
|
Flow : 23 to 55°C
|
7.0E-5
|
cm/cm/°C
|
|
|
Transverse : 23 to 55°C
|
7.0E-5
|
cm/cm/°C
|
| Additional Information |
Nominal Value
|
||
|
ISO Shortname
|
PC ASA
|