Terblend? S NM-31
Acrylonitrile Styrene Acrylate PA
Product Description:
Terblend? S is a UV-stabilized ASA/PA blend with high impact strength, easy flow and pronounced color fastness. It is especially suitable for unpainted highly UV-exposed automotive interior parts. FEATURES APPLICATIONS
| General | |
|
Material Status
|
|
|
Literature1
|
|
|
UL Yellow Card2
|
|
|
Search for UL Yellow Card
|
|
|
Availability
|
|
|
Additive
|
|
|
Features
|
|
|
Uses
|
|
|
Forms
|
|
|
Processing Method
|
| Physical | Dry | Conditioned |
Unit
|
Test Method
|
|
Density
|
1.07
|
--
|
g/cm3
|
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (240°C/10.0 kg)
|
60
|
--
|
cm3/10min
|
ISO 1133 |
|
Molding Shrinkage3
|
0.70
|
--
|
%
|
ISO 294-4 |
|
Water Absorption (Equilibrium, 23°C, 50% RH)
|
0.70
|
--
|
%
|
ISO 62 |
| Mechanical | Dry | Conditioned |
Unit
|
Test Method
|
|
Tensile Modulus
|
ISO 527-2 | |||
|
--
|
2100
|
--
|
MPa
|
|
|
23°C
|
--
|
1300
|
MPa
|
|
|
Tensile Stress (Yield, 23°C)
|
50.0
|
35.0
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Yield, 23°C)
|
3.3
|
7.0
|
%
|
ISO 527-2 |
|
Nominal Tensile Strain at Break (23°C)
|
25
|
50
|
%
|
ISO 527-2 |
|
Flexural Modulus (23°C)
|
2000
|
--
|
MPa
|
ISO 178 |
|
Flexural Stress (23°C)
|
65.0
|
--
|
MPa
|
ISO 178 |
| Impact | Dry | Conditioned |
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
|
-30°C
|
9.0
|
--
|
kJ/m2
|
|
|
23°C
|
70
|
--
|
kJ/m2
|
|
|
Notched Izod Impact Strength
|
ISO 180/A | |||
|
-30°C
|
8.0
|
--
|
kJ/m2
|
|
|
23°C
|
65
|
--
|
kJ/m2
|
| Thermal | Dry | Conditioned |
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
92.0
|
--
|
°C
|
ISO 75-2/B |
|
0.45 MPa, Annealed
|
97.0
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
65.0
|
--
|
°C
|
ISO 75-2/A |
|
1.8 MPa, Annealed
|
87.0
|
--
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
||||
|
--
|
110
|
--
|
°C
|
ISO 306/B50 |
|
--
|
205
|
--
|
°C
|
ISO 306/A50 |
|
CLTE - Flow
|
1.0E-4
|
--
|
cm/cm/°C
|
ISO 11359-2 |
| Electrical | Dry | Conditioned |
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E 14
|
--
|
ohms
|
IEC 60093 |
|
Volume Resistivity
|
1.0E 15
|
--
|
ohms·cm
|
IEC 60093 |
|
Relative Permittivity (1 MHz)
|
3.40
|
--
|
IEC 60250 | |
|
Dissipation Factor (1 MHz)
|
0.018
|
--
|
IEC 60250 | |
| Flammability | Dry | Conditioned |
Unit
|
Test Method
|
|
Flame Rating (1.5 mm)
|
HB
|
--
|
UL 94 |
| Injection |
Dry
|
Unit
|
|
|
Drying Temperature
|
80 to 90
|
°C
|
|
|
Drying Time
|
4.0 to 8.0
|
hr
|
|
|
Processing (Melt) Temp
|
240 to 270
|
°C
|
|
|
Mold Temperature
|
40 to 80
|
°C
|
| Notes |
| 1These links provide you with access to supplier literature. We work hard to keep them up to date; however you may find the most current literature from the supplier. |